Comparative analysis of the chemical and rheological curing kinetics of formaldehyde-based wood adhesives is crucial for assessing their respective performance. Differential scanning calorimetry (DSC) and rheometry are the conventional techniques used for monitoring the curing processes leading to crosslinking polymerization of the adhesives. However, the direct comparison of these techniques is inappropriate due to the intrinsic differences in their underlying procedures. To address this challenge, the two adhesive samples were sequentially cured, firstly with rheometry and followed by DSC. The observed higher curing degree in the subsequent DSC procedure underpins the incomplete curing of the samples during initial rheometry. Furthermore, the comparative assessment of the activation energies, molar ratios, and active groups of the two adhesives highlights the importance of the pre-exponential factor in addition to the activation energies, as it attributes to the probability of active groups coinciding at the appropriate spatial arrangement.
Hardboards (HBs) (wet-process high-density fibreboards) were made in an industrial trial using a binder system consisting of cationic mimosa tannin and laccase or just cationic tannin without any thermosetting adhesive. The boards displayed superior mechanical strength compared to reference boards made with phenol–formaldehyde, easily exceeding the European standards for general-purpose HBs. The thickness swell of most of the boards was slightly greater than the standards would allow, so some optimisation is required in this area. The improved board properties appear to be mainly associated with ionic interactions involving quaternary amino groups in cationic tannin and negatively charged wood fibres rather than to cross-linking of fibres via laccase-assisted formation and coupling of radicals in tannin and fibre lignin.