Clay minerals play an increasingly important role as functional fillers and reinforcing materials for clay polymer nanocomposites (CPN) in advanced applications. Among the prerequisites necessary for polymer improvement by clay minerals are homogeneous and stable Distribution of the clay mineral throughout the CPN, good compatibility of the reinforcement with the Matrix component and suitable processability. Typically, clay minerals are surface-modified with organic interface active compounds like detergents or silanes to obtain favorable properties as filler. They are incorporated into the polymer matrix using manufacturing Equipment like extruders, batch reactors or other mixing machines. In order for the surface modification to survive the stresses and strains during incorporation, the modified clay minerals must display sufficient thermal and mechanical stability to retain the compatibilizing effect. In the present study, thermogravimetry was used in combination with isoconversional kinetic analysis to determine the thermal stability of a silane-modified clay mineral based on bentonite. These findings were compared with the stability of the same clay mineral that was only surfactant-modified. It was found that silane modification leads to significantly improved thermal stability, which depends strongly on the type of silane employed.
This article contains data on the synthesis and mechanical characterization of polysiloxane-based urea-elastomers (PSUs) and is related to the research article entitled “Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application” (Riehle et al., 2018) [1]. These elastomers were prepared by a two-step polyaddition using the aliphatic diisocyanate 4,4′-Methylenbis(cyclohexylisocyanate) (H12MDI), a siloxane-based chain extender 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (APTMDS) and amino-terminated polydimethylsiloxanes (PDMS) or polydimethyl-methyl-phenyl-siloxane-copolymers (PDMS-Me,Ph), respectively. (More details about the synthesis procedure and the reaction scheme can be found in the related research article (Riehle et al., 2018) [1]).
Amino-terminated polydimethylsiloxanes with varying molecular weights and PDMS-Me,Ph-copolymers were prepared prior by a base-catalyzed ring-chain equilibration of a cyclic siloxane and the endblocker APTMDS. This DiB article contains a procedure for the synthesis of the base catalyst tetramethylammonium-3-aminopropyl-dimethylsilanolate and a generic synthesis procedure for the preparation of a PDMS having a targeted number average molecular weight of 3000 g mol−1. Molecular weights and the amount of methyl-phenyl-siloxane within the polysiloxane-copolymers were determined by 1H NMR and 29Si NMR spectroscopy. The corresponding NMR spectra and data are described in this article.
Additionally, this DiB article contains processed data on in line and off line FTIR-ATR spectroscopy, which was used to follow the reaction progress of the polyaddition by showing the conversion of the diisocyanate. All relevant IR band assignments of a polydimethylsiloxane-urea spectrum are described in this article.
Finally, data on the tensile properties and the mechanical hysteresis-behaviour at 100% elongation of PDMS-based polyurea-elastomers are shown in dependence to the PDMS molecular weight.