Natural wood colors occur within a wide range from almost white (e.g., white poplar), various yellowish, reddish, and brownish hues to almost black (e.g., ebony). The intrinsic color of wood is basically defined by its chemical composition. However, other factors such as specific anatomical formations or physical properties further affect the optical impression. Starting with the chemical composition of wood and anatomical basics, wood color and its modifications are discussed in this chapter. The classic method of coloring or re-coloring wood-based material surfaces is the application of a coating containing appropriate dyes or pigments. Different concepts for wood coating and coloration are presented. Another method used dyes for coloration of the wood structure. As alternative techniques, physical methods, for example, drying, steaming, ammoniation, bleaching, enzyme treatment, as well as treatment with electromagnetic irradiation (e.g., UV), are explained in this chapter.
Melamine-formaldehyde resins are widely used for decorative paper impregnation. Resin properties relevant for impregnation are mainly determined already at the stage of resin synthesis by the applied reaction conditions. Thus, understanding the relationship between reaction conditions and technological properties is important. Response surface methodology based on orthogonal parameter level variations is the most suitable tool to identify and quantify factor effects and deduce causal correlation patterns. Here, two major process factors of MF resin synthesis were systematically varied using such a statistical experimental design. To arrive at resins having a broad range of technological properties, initial pH and M:F ratio were varied in a wide range (pH: 7.9–12.1; M:F ratio: 1:1.5–1:4.5). The impregnation behavior of the resins was modeled using viscosity, penetration rate and residual curing capacity as technological responses. Based on the response surface models, nonlinear and synergistic action of process factors was quantified and a suitable process window for preparing resins with favorable impregnation performance was defined. It was found that low M:F ratios (~1:2–1:2.5) and comparatively high starting pHs (~pH 11) yield impregnation resins with rapid impregnation behavior and good residual curing capacity.
During curing of thermosetting resins the technologically relevant properties of binders and coatings develop. However, curing is difficult to monitor due to the multitude of chemical and physical processes taking place. Precise prediction of specific technological properties based on molecular properties is very difficult. In this study, the potential of principal component analysis (PCA) and principal component regression (PCR) in the analysis of Fourier transform infrared (FTIR) spectra is demonstrated using the example of melamine-formaldehyde (MF) resin curing in solid state. FTIR/PCA-based reaction trajectories are used to visualize the influence of temperature on isothermal cure. An FTIR/PCR model for predicting the hydrolysis resistance of cured MF resin from their spectral fingerprints is presented which illustrates the advantages of FTIR/PCR compared to the combination differential scanning calorimetry/isoconversional kinetic analysis. The presented methodology is transferable to the curing reactions of any thermosetting resin and can be applied to model other technologically relevant final properties as well.
Melamine–formaldehyde (MF) resins are widely used as adhesives and finishing materials in the wood industry. During resin cure, either methylene ether or methylene bridges are formed, leading to the formation of a three‐dimensional resin network. Not only the curing degree, but also the chemical species present in the cured resin determine the quality of the final product. Analytical methods allowing a detailed investigation of network formation are of great benefit to manufacturers. In the present work, resin cure of an MF precondensate is studied at different temperatures (100–200 °C) without considering the initial pH as a factor. Isoconversional kinetic analysis based on exothermal curing enthalpies enables calculation of the crosslinking degree at a given time/temperature regime. A semiquantitative determination of the chemical groups present is performed based on solid‐state nuclear magnetic resonance data. Fourier transform infrared spectroscopy has shown to be a fast and reliable analytical tool with high sensitivity toward functional groups and with great potential for at‐line process control.
Block-copolyesters of polyethylene terephthalate (PET) and polyethylene naphthalate (PEN) were synthesized via reactive extrusion. The influence of processing parameters on the material properties on a molecular scale like degree of trans-esterification, block length, and degree of randomness were investigated. The varied process factors were extrusion temperature and rotational speed. The effects of process parameter variation were investigated by 1H-NMR-spectroscopy. The experimental results show a clear dependence of the molecular properties on the processing conditions. By using statistical experimental design (DoE), it was possible to prepare defined copolyesters from PET and PEN without addition of further chemicals. With a degree of randomness between 0.05 and 0.5, the presence of an actual copolyester was confirmed when appropriate extrusion conditions were applied. The reactive extrusion process was confirmed to be suitable to produce defined block-copolyesters in a predictable and reproducible way. It was possible to produce designed sequence lengths, which could be adjusted within a range of 11–136 repeating units in the case of PET and, in the case of PEN, of 2.5–26. The produced materials can be used as barrier materials or barrier coatings to protect substrates against molecular oxygen and water vapour, e.g., in organic photovoltaic applications or food packaging. The described method is a one-pot alternative method to the previously described chemical recycling pathway.
The interfacial compatibility between polymers and nanoclay fillers as well as the thermostability of both components are important characteristics for processing them into polymer composites. While the polymer component is often grafted using common polymerization reactions, the nanoclay component is usually surface modified by surfactant treatment to improve compatibility. In the present study, the polymer ethylene vinyl alcohol and a nanoclay filler based on natural bentonite are both surface modified by different silanes, 3-glycidoxypropyltrimethoxysilane and methacryloxymethyltrimethoxysilane and their interfacial properties are investigated by inverse gas chromatography. The silane-modified samples had improved interfacial properties as reflected by a significant increase in dispersive and specific surface energies. Lewis acidities were determined using chloroform and 1,4-dioxane as polar probes and showed a good match between polymer and nanofiller interfaces. Lewis acidity was generally lower after silane-modification. Silanization yielded increased thermal stability of the treated samples. Thus, silanization led to improved compatibility and enhanced thermal stability which facilitates further processing.
Melamine formaldehyde (MF) resins are widely used for the gluing and surface coating of wood-based consumer products in the interior design of living environments. MF resins are especially relevant in decorative laminate applications because of their good performance-to-price ratio. In their industrial processing, an important intermediate state is the liquid MF prepolymer that is used for decorative paper impregnation. Here, the drying of impregnated papers is investigated with respect to premature curing. A new method to quantify water release upon drying that allows estimation of the degree of undesired precuring is described. Since curing proceeds via polycondensation, crosslinking brings about the release of water molecules. By thermogravimetric analysis (TGA), drying was studied in terms of water release due to physical drying (elimination of “dilution water”) and chemical crosslinking of the prepolymer to a three-dimensional MF network (elimination of chemically liberated water). The results obtained by TGA/IR spectroscopic analysis of the liberated volatiles show that the emission of water from b-stage MF can be clearly analytically separated into a physical (evaporation of dilution water) and a chemical (liberation via condensation) sequence. TGA experiments were correlated with curing experiments performed with differential scanning calorimetry (DSC) to estimate the residual crosslinking capacities of the impregnated papers. The drying conditions used during the preparation of impregnated decorative papers seemed to significantly affect their remaining reactivity only when harsh drying conditions were used. Upon heat exposure for prolonged time, precuring of the oligomer units results in a shift of the temperature maxima in TGA.
Ethylene terephthalate and ethylene naphthalate oligomers of defined degree of polymerization were synthesized via chemical recycling of the parent polymers. The oligomers were used as defined building blocks for the preparation of novel block-co-polyesters having tailored sequence compositions. The sequence lengths were systematically varied using Design of Experiments. The dispersive surface energy and the specific desorption energy of the co-polymers were determined by inverse gas chromatography. The study shows that polyethylene terephthalate-polyethylene naphthalate (PET-PEN) block-co-polyesters of defined sequence lengths can be prepared. Furthermore, the specific and dispersive surface energies of the obtained block-co-polyesters showed a linear dependence on the oligomer molecular weight and it was possible to regulate and control their interfacial properties. In contrast, with the corresponding random-block-co-polyesters no such dependence was found. The synthesized block-co-polyesters could be used as polymeric modifying agents for stabilizing PET-PEN polymer blends.
The intelligent recycling of plastics waste is a major concern. Because of the widespread use of polyethylene terephtalate, considerable amounts of PET waste are generated that are ideally re-introduced into the material cycle by generating second generation products without loss of materials performance. Chemical recycling methods are often expensive and entail environmentally hazardous by-products. Established mechanical methods generally provide materials of reduced quality, leading to products of lower quality. These drawbacks can be avoided by the development of new recycling methods that provide materials of high quality in every step of the production cycle. In the present work, oligomeric ethylene terephthalate with defined degrees of polymerization and defined molecular weight is produced by melt-mixing PET with different quantities of adipic acid as an alternative pathway of recycling PET with respect to conventional methods, offering ecofriendly and economical aspects. Additionally, block-copolyesters of defined block length are designed from the oligomeric products.
Decorative laminates based on melamine formaldehyde (MF) resin impregnated papers are used at great extent for surface finishing of engineered wood that is used for furniture, kitchen, and working surfaces, flooring and exterior cladding. In all these applications, optically flawless appearance is a major issue. The work described here is focused on enhancing the cleanability and antifingerprint properties of smooth, matt surface-finished melamine-coated particleboards for furniture fronts, without at the same time changing or deteriorating other important surface parameters such as hardness, roughness or gloss. In order to adjust the surface polarity of a low pressure melamine film, novel interface-active macromolecular compounds were prepared and tested for their suitability as an antifingerprint additive. Two hydroxy-functional surfactants (polydimethysiloxane, PDMS-OH and perfluoroether, PF-OH) were oxidized under mild conditions to the corresponding aldehydes (PDMS-CHO and PF-CHO) using a pyridinium chlorochromate catalyst. With the most promising oxidized polymeric additive, PDMS-CHO, the contact angles against water, n-hexadecane, and squalene increased from 79.8°, 26.3° and 31.4° for the pure MF surface to 108.5°, 54.8°, and 59.3°, respectively, for the modified MF surfaces. While for the laminated MF surface based on the oxidized fluoroether the gloss values were much higher than required, for the surfaces based on oxidized polydimethylsiloxane the technological values as well as the lower gloss values were in agreement with the requirements and showed much improved surface cleanability, as was also confirmed by colorimetric measurements.