The fiber deformations of once-dried, bleached and never-dried unbleached kraft pulps were studied with respect to their behavior in high- and low-consistency refining. The pulps were stained with congo red to experimentally highlight areas where the arrangement of the fibrils was altered by refining such as dislocated zones or slip planes. The stained fibers were analyzed with conventional Metso Fiberlab but also with a novel prototype measurement device utilizing a color imaging setup. The local intensity of the stain in the fiber was expressed as degree of overall damage (Overall fiber damage index, OFDI). The rewetted zero span tensile index (RWZSTI) was used to verify the OFDI with respect to the pulp strength. High consistency refining resulted in a clear increase in the number of kinks which negatively influenced the pulp strength. The OFDI which was used to detect the intensity of local fiber defects also responded accordingly. A higher OFDI resulted in a lower pulp strength. Low consistency refining removed a significant amount of kinks and resulted in an increase in fiber swelling. A slight increase in fibrillation and a significant increase in flake-like fines were also observed. The OFDI, however, was not reduced in low consistency refining as it would be expected by the removal of less severe dislocations. One reason proposed here is that low consistency refining created new fiber pores that allowed the dye to penetrate into the fiber wall similarly as it does in the zones of the dislocations.
Powder coating of engineered wood panels such as medium density fibreboards (MDF) is gaining industrial interest due to ecological and economic advantages of powder coating technology. For transferring powder coating technology to temperature-sensitive substrates like MDF, a thorough understanding of the melting, flowing and curing behaviour of the used low-bake resins is required. In the present study, thermo-analysis in combination with iso-conversional kinetic data analysis as well as rheometry is applied to characterise the properties of an epoxy-based powder coating. Neat resin and cured powder coating films are examined in order to define an ideal production window within which the resin is preferably applied and processed to yield satisfactory surface performance on the one hand and without exposing the carrier MDF too high a temperature load on the other hand to prevent the panel from deteriorating in mechanical strength. In order to produce powder coated films of high surface gloss – a feature that has not yet successfully been realized on MDF with powder coatings – a new curing technology, in-mould surface finishing, has been applied.
The powder coating of veneered particle boards by the sequence electrostatic powder application -powder curing via hot pressing is studied in order to create high gloss surfaces. To obtain an appealingaspect, veneer Sheets were glued by heat and pressure on top of particle boards and the resulting surfaceswere used as carrier substrates for powder coat finishing. Prior to the powder coating, the veneeredparticle board surfaces were pre-treated by sanding to obtain good uniformity and the boards werestored in a climate chamber at controlled temperature and humidity conditions to adjust an appropriate electrical surface resistance. Characterization of surface texture was done by 3D microscopy. The surfaceelectrical resistance was measured for the six veneers before and after their application on the particleboard surface. A transparent powder top-coat was applied electrostatically onto the veneered particleboard surface. Curing of the powder was done using a heated press at 130◦C for 8 min and a smooth, glossy coating was obtained on the veneered surfaces. By applying different amounts of powder thecoating thickness could be varied and the optimum amount of powder was determined for each veneer type.
Clay minerals play an increasingly important role as functional fillers and reinforcing materials for clay polymer nanocomposites (CPN) in advanced applications. Among the prerequisites necessary for polymer improvement by clay minerals are homogeneous and stable Distribution of the clay mineral throughout the CPN, good compatibility of the reinforcement with the Matrix component and suitable processability. Typically, clay minerals are surface-modified with organic interface active compounds like detergents or silanes to obtain favorable properties as filler. They are incorporated into the polymer matrix using manufacturing Equipment like extruders, batch reactors or other mixing machines. In order for the surface modification to survive the stresses and strains during incorporation, the modified clay minerals must display sufficient thermal and mechanical stability to retain the compatibilizing effect. In the present study, thermogravimetry was used in combination with isoconversional kinetic analysis to determine the thermal stability of a silane-modified clay mineral based on bentonite. These findings were compared with the stability of the same clay mineral that was only surfactant-modified. It was found that silane modification leads to significantly improved thermal stability, which depends strongly on the type of silane employed.
Homogeneous and monodispersed furan functionalised melamine-formaldehyde particles were produced. As a precursor, 2-chloro-1,3,5-triazine-2,4-diamine (Mel) was selectively substituted with 2-aminomethyl furan (Fu) units in a convenient one step reaction. The pure reaction product Fu-Mel, which was used without further purification, was reacted with formaldehyde by conventional sol-gel condensation in aqueous medium to yield chemically homogenous, spherically shaped and monodispersed particles. The particles were analysed using ATR-FT-IR, Raman, 1H and 13C NMR spectroscopy, TGA, SEM and DSC measurements. The reactivity of the furan groups located at the particle surface was studied by performing a thermoreversible Diels-Alder cycloaddition reaction with bis-maleimide coupling agents. The formed networks showed thermoreversible behaviour, which was characterised by dynamic IR and DSC measurements.
Here, we report the continuous peroxide-initiated grafting of vinyltrimethoxysilane (VTMS) onto a standard polyolefin by means of reactive extrusion to produce a functionalized liquid ethylene propylene copolymer (EPM). The effects of the process parameters governing the grafting reaction and their synergistic interactions are identified, quantified and used in a mathematical model of the extrusion process. As process variables the VTMS and peroxide concentrations and the extruder temperature setting were systematically studied for their influence on the grafting and the relative grafting degree using a face-centered central composite design (FCD). The grafting degree was quantified by 1H NMR spectroscopy. Response surface methodology (RSM) was used to calculate the most efficient grafting process in terms of chemical usage and graft yield. With the defined processing window, it was possible to make precise predictions about the grafting degree with at the same time highest possible relative degree of grafting.
Functionalised particles are highly requested in materials research, as they can be used as vital components in many advanced applications such as smart materials, functional coatings, drug carrier systems or adsorption materials. In this study, furan-functionalised melamine-formaldehyde (MF) particles were successfully prepared for the first time using an organic sol-gel process. Commercially available 2-Aminomethylfuran (AMF) and 2-Aminomethyl-5-methylfuran (AMMF) were used as modifying agents. In the isolated polymer particles, a melamine (M) to modifying agent ratio of M:AMF mol/mol 2.04:1 and M:AMMF ratio of mol/mol 1.25:1 was used. The obtained particles were isolated in various centrifugation and re-dispersion cycles and analysed using ATR-FT-IR, Raman and solid state 13C NMR spectroscopy, TGA, SEM and DSC measurements. Upon functionalisation the size of the MF particles increased (MF 1.59 µm, 27% CV (coefficient of variation); MF-AMF 2.56 µm, 25% CV; MF-AMMF 2.20 µm, 35% CV). DSC measurements showed that another type of exothermic residual reactivity besides condensation-based curing takes place with the furan-modified particles that is not related to the liberation of volatile compounds. The newly obtained particles are able to undergo Diels-Alder reactions with maleimide groups. The characteristic IR and Raman absorbance bands of the reaction products after the particles were reacted with 4,4′-Diphenylmethanebismaleimide reagent confirm the formation of a Diels-Alder adduct.
Impact of phenolic resin preparation on its properties and its penetration behavior in Kraft paper
(2018)
The core of decorative laminates is generally made of stacked Kraft paper sheets impregnated with a phenolic resin. As the impregnation process in industry is relatively fast, new methods need to be developed to characterize it for different paper-resin systems. Several phenolic resins were synthesized with the same Phenol:Formaldehyde ratio of 1:1.8 and characterized by Fourier Transform Infrared Spectrometry (FTIR) as well as Size-Exclusion Chromatography (SEC). In addition, their viscosities and surface tensions when diluted in methanol to 45% of solid content were measured. The capacity of each resin to penetrate a Kraft paper sheet was characterized using a new method, which measures the conductivities induced by the liquid resin crossing the paper substrate. With this method, crossing times could be measured with a good accuracy. Surprisingly, the results showed that the penetration time of the resin samples is not correlated to the viscosity values, but rather to the surface tension characteristics and the chemical characteristics of paper. Furthermore, some resins had a higher swelling effect on the fibers that delayed the crossing of the liquid through the paper.
A systematic study using a central composite design of experiments (DoE) was performed on the oxygen plasma surface modifications of two different polymers—Pellethane 2363-55DE, which is a polyurethane, and vinyltrimethoxysilane-grafted ethylene-propylene (EPR-g-VTMS), a cross-linked ethylene-propylene rubber. The impacts of four parameters—gas pressure, generator power, treatment duration, and process temperature—were assessed, with static contact angles and calculated surface free energies (SFEs) as the main responses in the DoE. The plasma effects on the surface roughness and chemistry were determined using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Through the sufficiently accurate DoE model evaluation, oxygen gas pressure was established as the most impactful factor, with the surface energy and polarity rising with falling oxygen pressure. Both polymers, though different in composition, exhibited similar modification trends in surface energy rise in the studied system. The SEM images showed a rougher surface topography after low pressure plasma treatments. XPS and subsequent multivariate data analysis of the spectra established that higher oxidized species were formed with plasma treatments at low oxygen pressures of 0.2 mbar.
The self-healing effect of melamine-based surfaces, triggered by temperature, was investigated. The temperature triggered reversible healing chemistry, on which the self-healing effect is based, was the Diels-Alder (DA) reaction between furan and malemeide groups. Melamine-furan containing building blocks were connected by multi-functional maleimide crosslinker via a Diels-Alder (DA) reaction to giva a DA adduct. The DA adduct was then reacted with formaldehyde to form a network by conventional condensation reaction of melamine amino groups with formaldehyde. The obtained resin was characterised and used for the impregnation of paper. Impregnated papers and neat resin werde used to perform scratch-healing tests and mechanical analysis of the novel coating system.