The powder coating of wood products as an emerging environmentally sustainable coating technology holds promise in terms of novel product quality features for engineered wood like medium-density fiberboards (MDFs). However, one major limitation currently impeding widespread application of powder coating technology is the availability of MDF panels that are suitable for this process. Typically, special-grade MDF panels are required that are more costly than standard-grade MDF panels to provide reliable coating quality, which makes powder coating economically unattractive for many users. Methods are needed that allow extending the range of available MDF grades. In the present study, three surface pretreatment approaches for MDFs were studied to increase the processability of standard-grade MDF in the powder coating process: atmospheric plasma pretreatment, infrared irradiation, and moisture equilibration in a climate chamber prior to electrostatic powder application. While atmospheric plasma treatment had no beneficial effect on the use of standard-grade MDF panels, both infrared preheating and preconditioning of the panels under controlled temperature–humidity conditions demonstrated that the range of MDF panels suitable for powder coating can be significantly extended by appropriate selection of the pretreatment procedure.
Homogeneous and monodispersed furan functionalised melamine-formaldehyde particles were produced. As a precursor, 2-chloro-1,3,5-triazine-2,4-diamine (Mel) was selectively substituted with 2-aminomethyl furan (Fu) units in a convenient one step reaction. The pure reaction product Fu-Mel, which was used without further purification, was reacted with formaldehyde by conventional sol-gel condensation in aqueous medium to yield chemically homogenous, spherically shaped and monodispersed particles. The particles were analysed using ATR-FT-IR, Raman, 1H and 13C NMR spectroscopy, TGA, SEM and DSC measurements. The reactivity of the furan groups located at the particle surface was studied by performing a thermoreversible Diels-Alder cycloaddition reaction with bis-maleimide coupling agents. The formed networks showed thermoreversible behaviour, which was characterised by dynamic IR and DSC measurements.
Functionalised particles are highly requested in materials research, as they can be used as vital components in many advanced applications such as smart materials, functional coatings, drug carrier systems or adsorption materials. In this study, furan-functionalised melamine-formaldehyde (MF) particles were successfully prepared for the first time using an organic sol-gel process. Commercially available 2-Aminomethylfuran (AMF) and 2-Aminomethyl-5-methylfuran (AMMF) were used as modifying agents. In the isolated polymer particles, a melamine (M) to modifying agent ratio of M:AMF mol/mol 2.04:1 and M:AMMF ratio of mol/mol 1.25:1 was used. The obtained particles were isolated in various centrifugation and re-dispersion cycles and analysed using ATR-FT-IR, Raman and solid state 13C NMR spectroscopy, TGA, SEM and DSC measurements. Upon functionalisation the size of the MF particles increased (MF 1.59 µm, 27% CV (coefficient of variation); MF-AMF 2.56 µm, 25% CV; MF-AMMF 2.20 µm, 35% CV). DSC measurements showed that another type of exothermic residual reactivity besides condensation-based curing takes place with the furan-modified particles that is not related to the liberation of volatile compounds. The newly obtained particles are able to undergo Diels-Alder reactions with maleimide groups. The characteristic IR and Raman absorbance bands of the reaction products after the particles were reacted with 4,4′-Diphenylmethanebismaleimide reagent confirm the formation of a Diels-Alder adduct.
The self-healing effect of melamine-based surfaces, triggered by temperature, was investigated. The temperature triggered reversible healing chemistry, on which the self-healing effect is based, was the Diels-Alder (DA) reaction between furan and malemeide groups. Melamine-furan containing building blocks were connected by multi-functional maleimide crosslinker via a Diels-Alder (DA) reaction to giva a DA adduct. The DA adduct was then reacted with formaldehyde to form a network by conventional condensation reaction of melamine amino groups with formaldehyde. The obtained resin was characterised and used for the impregnation of paper. Impregnated papers and neat resin werde used to perform scratch-healing tests and mechanical analysis of the novel coating system.
In der vorliegenden Studie werden typische, kommerziell erhältliche und mit unterschiedlichen Lacksystemen beschichtete MDF für den Küchenbereich hinsichtlich ihres Emissionsverhaltens und deren Oberflächeneigenschaften verglichen: wasserlack-, lösungsmittellack- und pulverlackbasierte Oberflächen. Es zeigt sich, dass eine Pulverlackierung insgesamt zu höherwertigen Produkten führt, sowohl in Bezug auf Kratzbeständigkeit, Haftung und Beständigkeit gegen feuchte Hitze als auch insbesondere in Bezug auf VOC-Emissionen. Die Wasserlackoberflächen schnitten hinsichtlich ihres Emissionsverhaltens deutlich besser ab als die lösemittelbasierten Beschichtungssysteme und zeigten in Bezug auf die Oberflächeneigenschaften mit einer Ausnahme vergleichbare Kennwerte.