DMOS transistors are often subject to high power dissipation and thus substantial self-heating. This limits their safe operating area because very high device temperatures can lead to thermal runaway and subsequent destruction. Because the peak temperature usually occurs only in a small region in the device, it is possible to redistribute part of the dissipated power from the hot region to the cooler device areas. In this way, the peak temperature is reduced, whereas the total power dissipation is still the same. Assuming that a certain temperature must not be exceeded for safe operation, the improved device is now capable of withstanding higher amounts of energy with an unchanged device area. This paper presents two simple methods to redistribute the power dissipation density and thus lower the peak device temperature. The presented methods only require layout changes. They can easily be applied to modern power technologies without the need of process modifications. Both methods are implemented in test structures and investigated by simulations and measurements.
DMOS transistors in integrated power technologies are often subject to significant self-heating and thus high temperatures, which can lead to device failure and reduced lifetime. Hence, it must be ensured that the device temperature does not rise too much. For this, the influence of the on-chip metallization must be taken into account because of the good thermal conductivity and significant thermal capacitance of the metal layers on top of the active DMOS area. In this paper, test structures with different metal layers and vias configurations are presented that can be used to determine the influence of the onchip metallization on the temperature caused by self-heating. It will be shown how accurate results can be obtained to determine even the influence of small changes in the metallization. The measurement results are discussed and explained, showing how on-chip metallization helps to lower the device temperature. This is further supported by numerical simulations. The obtained insights are valuable for technology optimization, but are also useful for calibration of temperature simulators.
On-chip metallization, especially in modern integrated BCD technologies, is often subject to high current densities and pronounced temperature cycles due to heat dissipation from power switches like LDMOS transistors. This paper continues the work on a sensor concept where small sense lines are embedded in the metallization layers above the active area of a switching LDMOS transistor. The sensors show a significant resistance change that correlates with the number of power cycles. Furthermore, influences of sense line layer, geometry and the dissipated energy are shown. In this paper, the focus lies on a more detailed analysis of the observed change in sense line resistance.
Modern power DMOS transistors greatly benefit from the continuous advances of the technology, which yield devices with very low area-specific RDS,on figures of merit and therefore allow for significantly reduced active areas. However, in many applications, where the devices must dissipate high amounts of energy and thus are subjected to significant self-heating, the active area is not dictated by RDS,on requirements, but by the energy constraints. In this paper, a simple method of improving the energy capability and reliability of power DMOS transistors operating in pulsed conditions is proposed and experimentally verified. The method consists in redistributing the power density from the hotter to the cooler device regions, hence achieving a more homogeneous temperature distribution and a reduced peak temperature. To demonstrate the principle, a simple gate offset circuit is used to redistribute the current density to the cooler DMOS parts. No technology changes are needed for the implementation, only minor changes to the driver circuit are necessary, with a minimal impact on the additional required active area. Improvements in the energy capability from 9.2% up to 39% have been measured. Furthermore, measurements have shown that the method remains effective also if the operating conditions change significantly. The simplicity and the effectiveness of the implementation makes the proposed method suitable to be used in a wide range of applications.
LDMOS transistors in integrated power technologies are often subject to thermo-mechanical stress, which degrades the on-chip metallization and eventually leads to a short. This paper investigates small sense lines embedded in the LDMOS metallization. It will be shown that their resistance depends strongly on the stress cycle number. Thus, they can be used as aging sensors and predict impending failures. Different test structures have been investigated to identify promising layout configurations. Such sensors are key components for resilient systems that adaptively reduce stress to allow aggressive LDMOS scaling without increasing the risk of failure.
This paper investigates the electrothermal stability and the predominant defect mechanism of a Schottky gate AlGaN/GaN HEMT. Calibrated 3-D electrothermal simulations are performed using a simple semiempirical dc model, which is verified against high-temperature measurements up to 440°C. To determine the thermal limits of the safe operating area, measurements up to destruction are conducted at different operating points. The predominant failure mechanism is identified to be hot-spot formation and subsequent thermal runaway, induced by large drain–gate leakage currents that occur at high temperatures. The simulation results and the high temperature measurements confirm the observed failure patterns.
Integrated power semiconductors are often used for applications with cyclic on-chip power dissipation. This leads to repetitive self-heating and thermo-mechanical stress, causing fatigue on the on-chip metallization and possibly destruction by short circuits. Because of this, an accurate simulation of the thermo-mechanical stress is needed already during the design phase to ensure that lifetime requirements are met. However, a detailed thermo mechanical simulation of the device, including the on-chip metallization is prohibitively time-consuming due to its complex structure, typically consisting of many thin metal lines with thousands of vias. This paper introduces a two-step approach as a solution for this problem. First, a simplified but fast simulation is performed to identify the device parts with the highest stress. After, precise simulations are carried out only for them. The applicability of this method is verified experimentally for LDMOS transistors with different metal configurations. The measured lifetimes and failure locations correlate well with the simulations. Moreover, a strong influence of the layout of the on-chip metallization lifetime was observed. This could also be explained with the simulation
method.
In many automotive applications, repetitive selfheating is the most critical operation condition for LDMOS transistors in smart power ICs. This is attributed to thermomechanical stress in the on-chip metallization, which results from the different thermal expansion coefficients of the metal and the intermetal dielectric. After many cycles, the accumulated strain in the metallization can lead to short circuits, thus limiting the lifetime. Increasing the LDMOS size can help to lower peak temperatures and therefore to reduce the stress. The downside of this is a higher cost. Hence, it has been suggested to use resilient systems that monitor the LDMOS metallization and lower the stress once a certain level of degradation is reached. Then, lifetime requirements can be fulfilled without oversizing LDMOS transistors, even though a certain performance loss has to be accepted. For such systems, suitable sensors for metal degradation are required. This work proposes a floating metal line embedded in the LDMOS metallization. The suitability of this approach has been investigated experimentally by test structures and shown to be a promising candidate. The obtained results will be explained by means of numerical thermo-mechanical simulations.