The powder coating of veneered particle boards by the sequence electrostatic powder application -powder curing via hot pressing is studied in order to create high gloss surfaces. To obtain an appealingaspect, veneer Sheets were glued by heat and pressure on top of particle boards and the resulting surfaceswere used as carrier substrates for powder coat finishing. Prior to the powder coating, the veneeredparticle board surfaces were pre-treated by sanding to obtain good uniformity and the boards werestored in a climate chamber at controlled temperature and humidity conditions to adjust an appropriate electrical surface resistance. Characterization of surface texture was done by 3D microscopy. The surfaceelectrical resistance was measured for the six veneers before and after their application on the particleboard surface. A transparent powder top-coat was applied electrostatically onto the veneered particleboard surface. Curing of the powder was done using a heated press at 130◦C for 8 min and a smooth, glossy coating was obtained on the veneered surfaces. By applying different amounts of powder thecoating thickness could be varied and the optimum amount of powder was determined for each veneer type.
Powder coatings provide several advantages over traditional coatings: environmental friendliness, freedom of design, robustness and resistance of surfaces, possibility to seamlessly all-around coating, fast production process, cost-effectiveness. In the last years these benefits of the powder coating technology have been adopted from metal to heat-sensitive natural fibre/ wood based substrates (especially medium density fibre boards- MDF) used for interior furniture applications. Powder coated MDF furniture parts are gaining market share already in the classic furniture applications kitchen, bathroom, living and offices. The acceptance of this product is increasing as reflected by excellent growth rates and an increasing customer base. Current efforts of the powder coating industry to develop new powders with higher reactivity (i.e. lower curing temperatures and shorter curing times; e.g. 120°C/5min) will enable the powder coating of other heat-sensitive substrates like natural fibre composites, wood plastic composites, light weight panels and different plastics in the future. The coating could be applied and cured by the conventional powder coating process (electrostatic application, and melting and curing in an IR-oven) or by a new powder coating procedure based on the in-mould-coating (IMC) technique which is already established in the plastic industry. Extra value could be added in the future by the functional powder toner printing of powder coated substrates using the electrophotographic printing technology, meeting the future demand of both individualization of the furniture part surface by applying functional 3D textures and patterns and individually created coloured images and enabling shorter delivery times for these individualized parts. The paper describes the distinctiveness of powder coating on natural fibre/ wood based substrates, the requirements of the substrate and the coating powder.
In the powder coating of veneered particle boards the highly reactive hybrid epoxy/polyester powder transparent Drylac 530 Series from TIGER Coatings GmbH & Co. KG, Wels, Austria was used. Curing is accelerated by a mixture of catalysts reaching curing times of 3 min at 150 °C or 5 min at 135 °C which allows for energy and time savings making Drylac Series 530 powder suitable for the coating of temperaturesensitive substrates such as MDF and wood.