Properties data of phenolic resins synthetized for the impregnation of saturating Kraft paper
(2018)
The quality of decorative laminates boards depends on the impregnation process of Kraft papers with a phenolic resin,which constitute the raw materials for the manufacture of the cores of such boards.In the laminates industries,the properties of resins are adapted via their syntheses,usually by mixing phenol and formaldehyde in a batch,where additives,temperature and stirring parameters can be controlled. Therefore, many possibilities of preparation and phenolic resins exist, that leads to different combinations of physico chemical properties. In this article, the properties data of eight phenolic resins synthetized with different parameters of pH and reaction times at 60 °C and 90 °C are presented: the losses of pH after synthesis and the dynamic viscosities measured after synthesis and one the solid content is adjusted to 45%w/w in methanol. Data aquired by Differential Scanning Calorimetry (DSC) of the resins and Inverse Gas Chromatography (IGC) of cured solids are given as well.
A series of novel biomedical TPCUs with different percentages of hard segment and a silicone component in the soft segment were synthesized in a multi stage one-pot method. The kinetic profiles of the urethane formation in TPCU-based copolymer systems were monitored by rheological, in line FTIR spectroscopic (React IR) and real-time calorimetric (RC1) methods. This process-analytically monitored multi step synthesis was successfully used to optimize the production of medical-grade TPCU elastomers on preparative scale (in lots of several kg) with controlled molecular structure and mechanical properties. Various surface and bulk analytical methods as well as systematic studies of the mechanic response of the elastomer end-products towards compression and tensile loading were used to estimate the bio-stability of the prepared TPCUs in vitro after 3 months. The tests suggested that high bio-stability of all polyurethane formulations using accelerating in vitro test can be attributed to the synthetic design as well as to the specific techniques used for specimen preparation, namely: (1) the annealing for reducing residual polymer surface stress and preventing IES, (2) stabilization of the morphology by long time storage of the specimens after processing before being immersed in the test liquids, (3) purification by extraction to remove the shot chain oligomers which are the most susceptible to degradation. All mechanical tests were performed on cylindrical and circular disc specimens for modelling the thickness of the meniscus implants under application-relevant stress conditions.
This article contains data on the synthesis and mechanical characterization of polysiloxane-based urea-elastomers (PSUs) and is related to the research article entitled “Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application” (Riehle et al., 2018) [1]. These elastomers were prepared by a two-step polyaddition using the aliphatic diisocyanate 4,4′-Methylenbis(cyclohexylisocyanate) (H12MDI), a siloxane-based chain extender 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (APTMDS) and amino-terminated polydimethylsiloxanes (PDMS) or polydimethyl-methyl-phenyl-siloxane-copolymers (PDMS-Me,Ph), respectively. (More details about the synthesis procedure and the reaction scheme can be found in the related research article (Riehle et al., 2018) [1]).
Amino-terminated polydimethylsiloxanes with varying molecular weights and PDMS-Me,Ph-copolymers were prepared prior by a base-catalyzed ring-chain equilibration of a cyclic siloxane and the endblocker APTMDS. This DiB article contains a procedure for the synthesis of the base catalyst tetramethylammonium-3-aminopropyl-dimethylsilanolate and a generic synthesis procedure for the preparation of a PDMS having a targeted number average molecular weight of 3000 g mol−1. Molecular weights and the amount of methyl-phenyl-siloxane within the polysiloxane-copolymers were determined by 1H NMR and 29Si NMR spectroscopy. The corresponding NMR spectra and data are described in this article.
Additionally, this DiB article contains processed data on in line and off line FTIR-ATR spectroscopy, which was used to follow the reaction progress of the polyaddition by showing the conversion of the diisocyanate. All relevant IR band assignments of a polydimethylsiloxane-urea spectrum are described in this article.
Finally, data on the tensile properties and the mechanical hysteresis-behaviour at 100% elongation of PDMS-based polyurea-elastomers are shown in dependence to the PDMS molecular weight.