Background/Aim: The aim of this study was the conception, production, material analysis and cytocompatibility analysis of a new collagen foam for medical applications. Materials and Methods: After the innovative production of various collagen sponges from bovine sources, the foams were analyzed ex vivo in terms of their structure (including pore size) and in vitro in terms of cytocompatibility according to EN ISO 10993-5/-12. In vitro, the collagen foams were compared with the established soft and hard tissue materials cerabone and Jason membrane (both botiss biomaterials GmbH, Zossen, Germany). Results: Collagen foams with different compositions were successfully produced from bovine sources. Ex vivo, the foams showed a stable and long-lasting primary structure quality with a bubble area of 1,000 to 2,000 μm2. In vitro, all foams showed sufficient cytocompatibility. Conclusion: Collagen sponges represent a promising material for hard and soft tissue regeneration. Future studies could focus on integrating and investigating different additives in the foams.
Background/Aim: The aim of this study was the development of a new osteoconductivity index to determine the bone healing capacities of bone substitute materials (BSM) on the basis of 3D microcomputed tomographic (μ-CT) data. Materials and Methods: Sinus biopsies were used for the comparative analysis of the integration behavior of two xenogeneic BSM (cerabone® and Bio Oss®). 3D μ-CT and data sets from histomorphometrical measurements based on 2D histological slices were used to measure the bone-material-contact and the tissue distribution within the biopsies. The tissue reactions to both BSM were microscopically analyzed. Results: The 3D and 2D results of the osteoconductivity measurements showed comparable material-bone contacts for both BSM, but the 2D data were significantly lower. The same results were found when tissue distribution was measured in both groups. The histopathological analysis showed comparative tissue reactions in both BSM. Conclusion: Osteoconductivity index is a reliable measurement parameter for determining the healing capacities of BSM. The observed differences between both measurement methods could be assigned to the resolution capacity of μ-CT data that did not allow for a precise interface distinction between both BSM and bone tissue. Histomorphometrical data based on histological slides still allow for a more exact evaluation.
This review gives a short overview of the physical processes involved in the formation of the polyelectrolyte multilayers (PEMs) and their destruction. These two processes are vital for the formation of PEMs with desired physical and chemical structures, and for loading them with active substances and their spatial controlled release. It includes a survey of the physical and chemical properties that are key points for controlling film nanostructure in relation to biological processes and different possibilities for controlling cell behavior by means of film composition, bioactivity, mechanical properties, and three-dimensional organization.
Positively charged metallic oxides prevent blood coagulation whereas negatively charged metallic oxides are thrombogenic. This study was performed to examine whether this effect extends to metallic oxide nanoparticles. Oscillation shear rheometry was used to study the effect of zinc oxide and silicon dioxide nanoparticles on thrombus formation in human whole blood. Our data show that oscillation shear rheometry is a sensitive and robust technique to analyze thrombogenicity induced by nanoparticles. Blood without previous contact with nanoparticles had a clotting time (CT) of 16.7 ± 1.0 min reaching a maximal clot strength (CS) of 16 ± 14 Pa (G') after 30 min. ZnO nanoparticles (diameter 70 nm, +37 mV zeta-potential) at a concentration of 1 mg/mL prolonged CT to 20.8 ± 3.6 min and provoked a weak clot (CS 1.5 ± 1.0 Pa). However, at a lower concentration of 100 µg/mL the ZnO particles dramatically reduced CT to 6.0 ± 0.5 min and increased CS to 171 ± 63 Pa. This procoagulant effect decreased at lower concentrations reaching the detection limit at 10 ng/mL. SiO2 nanoparticles (diameter 232 nm, −28 mV zeta-potential) at high concentrations (1 mg/mL) reduced CT (2.1 ± 0.2 min) and stimulated CS (249 ± 59 Pa). Similar to ZnO particles, this procoagulant effect reached a detection limit at 10 ng/mL. Nanoparticles in high concentrations reproduce the surface charge effects on blood coagulation previously observed with large particles or solid metal oxides. However, nanoparticles with different surface charges equally well stimulate coagulation at lower concentrations. This stimulation may be an effect which is not directly related to the surface charge.