670 Industrielle und handwerkliche Fertigung
Refine
Document Type
- Journal article (10)
- Book chapter (1)
- Conference proceeding (1)
Is part of the Bibliography
- yes (12)
Institute
- Life Sciences (12)
Publisher
- Elsevier (5)
- Springer (2)
- ACS (1)
- CRC Press (1)
- Institut für Holztechnologie (1)
- Taylor & Francis (1)
- Technical Conference Management (1)
Porous silica materials are often used for drug delivery. However, systems for simultaneous delivery of multiple drugs are scarce. Here we show that anisotropic and amphiphilic dumbbell core–shell silica microparticles with chemically selective environments can entrap and release two drugs simultaneously. The dumbbells consist of a large dense lobe and a smaller hollow hemisphere. Electron microscopy images show that the shells of both parts have mesoporous channels. In a simple etching process, the properly adjusted stirring speed and the application of ammonium fluoride as etching agent determine the shape and the surface anisotropy of the particles. The surface of the dense lobe and the small hemisphere differ in their zeta potentials consistent with differences in dye and drug entrapment. Confocal Raman microscopy and spectroscopy show that the two polyphenols curcumin (Cur) and quercetin (QT) accumulate in different compartments of the particles. The overall drug entrapment efficiency of Cur plus QT is high for the amphiphilic particles but differs widely between Cur and QT compared to controls of core–shell silica microspheres and uniformly charged dumbbell microparticles. Furthermore, Cur and QT loaded microparticles show different cancer cell inhibitory activities. The highest activity is detected for the dual drug loaded amphiphilic microparticles in comparison to the controls. In the long term, amphiphilic particles may open up new strategies for drug delivery.
A systematic study using a central composite design of experiments (DoE) was performed on the oxygen plasma surface modifications of two different polymers—Pellethane 2363-55DE, which is a polyurethane, and vinyltrimethoxysilane-grafted ethylene-propylene (EPR-g-VTMS), a cross-linked ethylene-propylene rubber. The impacts of four parameters—gas pressure, generator power, treatment duration, and process temperature—were assessed, with static contact angles and calculated surface free energies (SFEs) as the main responses in the DoE. The plasma effects on the surface roughness and chemistry were determined using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Through the sufficiently accurate DoE model evaluation, oxygen gas pressure was established as the most impactful factor, with the surface energy and polarity rising with falling oxygen pressure. Both polymers, though different in composition, exhibited similar modification trends in surface energy rise in the studied system. The SEM images showed a rougher surface topography after low pressure plasma treatments. XPS and subsequent multivariate data analysis of the spectra established that higher oxidized species were formed with plasma treatments at low oxygen pressures of 0.2 mbar.
Homogeneous and monodispersed furan functionalised melamine-formaldehyde particles were produced. As a precursor, 2-chloro-1,3,5-triazine-2,4-diamine (Mel) was selectively substituted with 2-aminomethyl furan (Fu) units in a convenient one step reaction. The pure reaction product Fu-Mel, which was used without further purification, was reacted with formaldehyde by conventional sol-gel condensation in aqueous medium to yield chemically homogenous, spherically shaped and monodispersed particles. The particles were analysed using ATR-FT-IR, Raman, 1H and 13C NMR spectroscopy, TGA, SEM and DSC measurements. The reactivity of the furan groups located at the particle surface was studied by performing a thermoreversible Diels-Alder cycloaddition reaction with bis-maleimide coupling agents. The formed networks showed thermoreversible behaviour, which was characterised by dynamic IR and DSC measurements.
Impact of phenolic resin preparation on its properties and its penetration behavior in Kraft paper
(2018)
The core of decorative laminates is generally made of stacked Kraft paper sheets impregnated with a phenolic resin. As the impregnation process in industry is relatively fast, new methods need to be developed to characterize it for different paper-resin systems. Several phenolic resins were synthesized with the same Phenol:Formaldehyde ratio of 1:1.8 and characterized by Fourier Transform Infrared Spectrometry (FTIR) as well as Size-Exclusion Chromatography (SEC). In addition, their viscosities and surface tensions when diluted in methanol to 45% of solid content were measured. The capacity of each resin to penetrate a Kraft paper sheet was characterized using a new method, which measures the conductivities induced by the liquid resin crossing the paper substrate. With this method, crossing times could be measured with a good accuracy. Surprisingly, the results showed that the penetration time of the resin samples is not correlated to the viscosity values, but rather to the surface tension characteristics and the chemical characteristics of paper. Furthermore, some resins had a higher swelling effect on the fibers that delayed the crossing of the liquid through the paper.
Functionalised particles are highly requested in materials research, as they can be used as vital components in many advanced applications such as smart materials, functional coatings, drug carrier systems or adsorption materials. In this study, furan-functionalised melamine-formaldehyde (MF) particles were successfully prepared for the first time using an organic sol-gel process. Commercially available 2-Aminomethylfuran (AMF) and 2-Aminomethyl-5-methylfuran (AMMF) were used as modifying agents. In the isolated polymer particles, a melamine (M) to modifying agent ratio of M:AMF mol/mol 2.04:1 and M:AMMF ratio of mol/mol 1.25:1 was used. The obtained particles were isolated in various centrifugation and re-dispersion cycles and analysed using ATR-FT-IR, Raman and solid state 13C NMR spectroscopy, TGA, SEM and DSC measurements. Upon functionalisation the size of the MF particles increased (MF 1.59 µm, 27% CV (coefficient of variation); MF-AMF 2.56 µm, 25% CV; MF-AMMF 2.20 µm, 35% CV). DSC measurements showed that another type of exothermic residual reactivity besides condensation-based curing takes place with the furan-modified particles that is not related to the liberation of volatile compounds. The newly obtained particles are able to undergo Diels-Alder reactions with maleimide groups. The characteristic IR and Raman absorbance bands of the reaction products after the particles were reacted with 4,4′-Diphenylmethanebismaleimide reagent confirm the formation of a Diels-Alder adduct.
Soft thermoplastic polysiloxane-urea-elastomers (PSUs) were prepared for the application as a biomaterial to replace the human natural lens after cataract surgery. PSUs were synthesized from amino-terminated polydimethylsiloxanes (PDMS), 4,4′-Methylenebis(cyclohexylisocyanate) (H12MDI) and 1,3–Bis(3-aminopropyl)-1,1,3,3–tetramethyldisiloxane (APTMDS) by a two-step polyaddition route. Such a material has to be highly transparent and must exhibit a low Young’s Modulus and excellent dimensional stability. Polydimethylsiloxanes in the range of 3000–33,000 g·mol−1 were therefore prepared by ring-chain-equilibration of octamethylcyclotetrasiloxane (D4) and APTMDS in order to study the influence of the soft segment molecular weight on the mechanical properties and the transparency of the PSU-elastomers. 2,4,6,8-Tetramethyl-2,4,6,8-tetraphenylcyclotetrasiloxane (D4Me,Ph) was co-polymerized with D4 in order to adjust the refractive index of the polydimethyl-methyl-phenyl-siloxane-copolymers to a value equivalent to a young human natural lens. Very elastic PSUs with Elongation at Break values higher than 700% were prepared. PSU-elastomers, synthesized from PDMS of molecular weights up to 18,000 g·mol−1, showed transmittance values of over 90% within the visible spectrum range. The soft segment refractive index was increased through the incorporation of 14 mol % of methyl-phenyl-siloxane from 1.4011 to 1.4346 (37 °C). Young’s Moduli of PSU-elastomers were around 1 MPa and lower at PDMS molecular weights up to 15,000 g·mol−1. 10-cycle hysteresis measurements were applied to evaluate the mechanical stability of the PSUs at repeated stress. Hysteresis values at 100% strain decreased from 32 to 2% (10th cycle) with increasing PDMS molecular weight. Furthermore, hysteresis at 5% strain was only detected in PSU-elastomers with low PDMS molecular weights. Finally, preliminary results of in vitro cytotoxicity tests on a PSU-elastomer showed no toxic effects on HaCaT-cells.
This article provides a general overview of the most promising candidates of bio based materials and deals with the most important issues when it comes to their incorporation into PF resins. Due to their abundance on Earth, much knowledge of lignin-based materials has already been gained and uses of lignin in PF resins have been studied for many decades. Other natural polyphenols that are less frequently considered for impregnation are covered as well, as they do also possess some potential for PF substitution.
High quality decorative laminate panels typically consist of two major types of components: the surface layers comprising décor and overlay papers that are impregnated with melamine-based resins, and the core which is made of stacks of kraft papers impregnated with phenolic (PF) resin. The PF-impregnated layers impart superior hydrolytic stability, mechanical strength and fire-resistance to the composite. The manufacturing involves the complex interplay between resin, paper and impregnation/drying processes. Changes in the input variables cause significant alterations in the process characteristics and adaptations of the used materials and specific process conditions may, in turn, be required. This review summarizes the main variables influencing both processability and technological properties of phenolic resin impregnated papers and laminates produced therefrom. It is aimed at presenting the main influences from the involved components (resin and paper), how these may be controlled during the respective process steps (resin preparation and paper production), how they influence the impregnation and lamination conditions, how they affect specific aspects of paper and laminate performance, and how they interact with each other
(synergies).
In der vorliegenden Studie werden typische, kommerziell erhältliche und mit unterschiedlichen Lacksystemen beschichtete MDF für den Küchenbereich hinsichtlich ihres Emissionsverhaltens und deren Oberflächeneigenschaften verglichen: wasserlack-, lösungsmittellack- und pulverlackbasierte Oberflächen. Es zeigt sich, dass eine Pulverlackierung insgesamt zu höherwertigen Produkten führt, sowohl in Bezug auf Kratzbeständigkeit, Haftung und Beständigkeit gegen feuchte Hitze als auch insbesondere in Bezug auf VOC-Emissionen. Die Wasserlackoberflächen schnitten hinsichtlich ihres Emissionsverhaltens deutlich besser ab als die lösemittelbasierten Beschichtungssysteme und zeigten in Bezug auf die Oberflächeneigenschaften mit einer Ausnahme vergleichbare Kennwerte.
In the powder coating of veneered particle boards the highly reactive hybrid epoxy/polyester powder transparent Drylac 530 Series from TIGER Coatings GmbH & Co. KG, Wels, Austria was used. Curing is accelerated by a mixture of catalysts reaching curing times of 3 min at 150 °C or 5 min at 135 °C which allows for energy and time savings making Drylac Series 530 powder suitable for the coating of temperaturesensitive substrates such as MDF and wood.