Clay minerals play an increasingly important role as functional fillers and reinforcing materials for clay polymer nanocomposites (CPN) in advanced applications. Among the prerequisites necessary for polymer improvement by clay minerals are homogeneous and stable Distribution of the clay mineral throughout the CPN, good compatibility of the reinforcement with the Matrix component and suitable processability. Typically, clay minerals are surface-modified with organic interface active compounds like detergents or silanes to obtain favorable properties as filler. They are incorporated into the polymer matrix using manufacturing Equipment like extruders, batch reactors or other mixing machines. In order for the surface modification to survive the stresses and strains during incorporation, the modified clay minerals must display sufficient thermal and mechanical stability to retain the compatibilizing effect. In the present study, thermogravimetry was used in combination with isoconversional kinetic analysis to determine the thermal stability of a silane-modified clay mineral based on bentonite. These findings were compared with the stability of the same clay mineral that was only surfactant-modified. It was found that silane modification leads to significantly improved thermal stability, which depends strongly on the type of silane employed.
A systematic study using a central composite design of experiments (DoE) was performed on the oxygen plasma surface modifications of two different polymers—Pellethane 2363-55DE, which is a polyurethane, and vinyltrimethoxysilane-grafted ethylene-propylene (EPR-g-VTMS), a cross-linked ethylene-propylene rubber. The impacts of four parameters—gas pressure, generator power, treatment duration, and process temperature—were assessed, with static contact angles and calculated surface free energies (SFEs) as the main responses in the DoE. The plasma effects on the surface roughness and chemistry were determined using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Through the sufficiently accurate DoE model evaluation, oxygen gas pressure was established as the most impactful factor, with the surface energy and polarity rising with falling oxygen pressure. Both polymers, though different in composition, exhibited similar modification trends in surface energy rise in the studied system. The SEM images showed a rougher surface topography after low pressure plasma treatments. XPS and subsequent multivariate data analysis of the spectra established that higher oxidized species were formed with plasma treatments at low oxygen pressures of 0.2 mbar.
Soft thermoplastic polysiloxane-urea-elastomers (PSUs) were prepared for the application as a biomaterial to replace the human natural lens after cataract surgery. PSUs were synthesized from amino-terminated polydimethylsiloxanes (PDMS), 4,4′-Methylenebis(cyclohexylisocyanate) (H12MDI) and 1,3–Bis(3-aminopropyl)-1,1,3,3–tetramethyldisiloxane (APTMDS) by a two-step polyaddition route. Such a material has to be highly transparent and must exhibit a low Young’s Modulus and excellent dimensional stability. Polydimethylsiloxanes in the range of 3000–33,000 g·mol−1 were therefore prepared by ring-chain-equilibration of octamethylcyclotetrasiloxane (D4) and APTMDS in order to study the influence of the soft segment molecular weight on the mechanical properties and the transparency of the PSU-elastomers. 2,4,6,8-Tetramethyl-2,4,6,8-tetraphenylcyclotetrasiloxane (D4Me,Ph) was co-polymerized with D4 in order to adjust the refractive index of the polydimethyl-methyl-phenyl-siloxane-copolymers to a value equivalent to a young human natural lens. Very elastic PSUs with Elongation at Break values higher than 700% were prepared. PSU-elastomers, synthesized from PDMS of molecular weights up to 18,000 g·mol−1, showed transmittance values of over 90% within the visible spectrum range. The soft segment refractive index was increased through the incorporation of 14 mol % of methyl-phenyl-siloxane from 1.4011 to 1.4346 (37 °C). Young’s Moduli of PSU-elastomers were around 1 MPa and lower at PDMS molecular weights up to 15,000 g·mol−1. 10-cycle hysteresis measurements were applied to evaluate the mechanical stability of the PSUs at repeated stress. Hysteresis values at 100% strain decreased from 32 to 2% (10th cycle) with increasing PDMS molecular weight. Furthermore, hysteresis at 5% strain was only detected in PSU-elastomers with low PDMS molecular weights. Finally, preliminary results of in vitro cytotoxicity tests on a PSU-elastomer showed no toxic effects on HaCaT-cells.
Here, we report the continuous peroxide-initiated grafting of vinyltrimethoxysilane (VTMS) onto a standard polyolefin by means of reactive extrusion to produce a functionalized liquid ethylene propylene copolymer (EPM). The effects of the process parameters governing the grafting reaction and their synergistic interactions are identified, quantified and used in a mathematical model of the extrusion process. As process variables the VTMS and peroxide concentrations and the extruder temperature setting were systematically studied for their influence on the grafting and the relative grafting degree using a face-centered central composite design (FCD). The grafting degree was quantified by 1H NMR spectroscopy. Response surface methodology (RSM) was used to calculate the most efficient grafting process in terms of chemical usage and graft yield. With the defined processing window, it was possible to make precise predictions about the grafting degree with at the same time highest possible relative degree of grafting.
This article contains data on the synthesis and mechanical characterization of polysiloxane-based urea-elastomers (PSUs) and is related to the research article entitled “Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application” (Riehle et al., 2018) [1]. These elastomers were prepared by a two-step polyaddition using the aliphatic diisocyanate 4,4′-Methylenbis(cyclohexylisocyanate) (H12MDI), a siloxane-based chain extender 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (APTMDS) and amino-terminated polydimethylsiloxanes (PDMS) or polydimethyl-methyl-phenyl-siloxane-copolymers (PDMS-Me,Ph), respectively. (More details about the synthesis procedure and the reaction scheme can be found in the related research article (Riehle et al., 2018) [1]).
Amino-terminated polydimethylsiloxanes with varying molecular weights and PDMS-Me,Ph-copolymers were prepared prior by a base-catalyzed ring-chain equilibration of a cyclic siloxane and the endblocker APTMDS. This DiB article contains a procedure for the synthesis of the base catalyst tetramethylammonium-3-aminopropyl-dimethylsilanolate and a generic synthesis procedure for the preparation of a PDMS having a targeted number average molecular weight of 3000 g mol−1. Molecular weights and the amount of methyl-phenyl-siloxane within the polysiloxane-copolymers were determined by 1H NMR and 29Si NMR spectroscopy. The corresponding NMR spectra and data are described in this article.
Additionally, this DiB article contains processed data on in line and off line FTIR-ATR spectroscopy, which was used to follow the reaction progress of the polyaddition by showing the conversion of the diisocyanate. All relevant IR band assignments of a polydimethylsiloxane-urea spectrum are described in this article.
Finally, data on the tensile properties and the mechanical hysteresis-behaviour at 100% elongation of PDMS-based polyurea-elastomers are shown in dependence to the PDMS molecular weight.
Film formation of self synthesized Polymer EPM–g–VTMDS (ethylene–propylene rubber, EPM, grafted with vinyltetramethyldisiloxane, VTMDS) was studied regarding bonding to adhesion promoter vinyltrimethoxysilane (VTMS) on oxidized 18/10 chromium/nickel–steel (V2A) stainless steel surfaces. Polymer films of different mixed solutions including commercial siloxane and silicone, dimethyl, vinyl group terminated crosslinker (HANSA SFA 42100, CAS# 68083-19-2, 0.35 mmol Vinyl/g) and platinum, 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complex Karstedt's catalyst (ALPA–KAT 1, CAS# 68478-92-2) were spin coated on V2A stainless steel surfaces with adsorbed VTMS thin layers in order to analyze film formation of EPM–g–VTMDS at early stages. Surface topography and chemical bonding of the high performance polymers on different oxidized V2A surfaces were investigated with X–ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and surface enhanced Raman spectroscopy (SERS). AFM and SEM as well as XPS results indicated that the formation of the polymer film proceeds via growth of polymer islands. Chemical signatures of the essential polymer contributions, linker and polymer backbones, could be identified using XPS core level peak shape analysis and also SERS. The appearance of signals which are related to Si–O–Si can be seen as a clear indication of lateral crosslinking and silica network formation in the films on the V2A surface.