Decorative laminates based on melamine formaldehyde (MF) resin impregnated papers are used at great extent for surface finishing of engineered wood that is used for furniture, kitchen, and working surfaces, flooring and exterior cladding. In all these applications, optically flawless appearance is a major issue. The work described here is focused on enhancing the cleanability and antifingerprint properties of smooth, matt surface-finished melamine-coated particleboards for furniture fronts, without at the same time changing or deteriorating other important surface parameters such as hardness, roughness or gloss. In order to adjust the surface polarity of a low pressure melamine film, novel interface-active macromolecular compounds were prepared and tested for their suitability as an antifingerprint additive. Two hydroxy-functional surfactants (polydimethysiloxane, PDMS-OH and perfluoroether, PF-OH) were oxidized under mild conditions to the corresponding aldehydes (PDMS-CHO and PF-CHO) using a pyridinium chlorochromate catalyst. With the most promising oxidized polymeric additive, PDMS-CHO, the contact angles against water, n-hexadecane, and squalene increased from 79.8°, 26.3° and 31.4° for the pure MF surface to 108.5°, 54.8°, and 59.3°, respectively, for the modified MF surfaces. While for the laminated MF surface based on the oxidized fluoroether the gloss values were much higher than required, for the surfaces based on oxidized polydimethylsiloxane the technological values as well as the lower gloss values were in agreement with the requirements and showed much improved surface cleanability, as was also confirmed by colorimetric measurements.
The intelligent recycling of plastics waste is a major concern. Because of the widespread use of polyethylene terephtalate, considerable amounts of PET waste are generated that are ideally re-introduced into the material cycle by generating second generation products without loss of materials performance. Chemical recycling methods are often expensive and entail environmentally hazardous by-products. Established mechanical methods generally provide materials of reduced quality, leading to products of lower quality. These drawbacks can be avoided by the development of new recycling methods that provide materials of high quality in every step of the production cycle. In the present work, oligomeric ethylene terephthalate with defined degrees of polymerization and defined molecular weight is produced by melt-mixing PET with different quantities of adipic acid as an alternative pathway of recycling PET with respect to conventional methods, offering ecofriendly and economical aspects. Additionally, block-copolyesters of defined block length are designed from the oligomeric products.
Ethylene terephthalate and ethylene naphthalate oligomers of defined degree of polymerization were synthesized via chemical recycling of the parent polymers. The oligomers were used as defined building blocks for the preparation of novel block-co-polyesters having tailored sequence compositions. The sequence lengths were systematically varied using Design of Experiments. The dispersive surface energy and the specific desorption energy of the co-polymers were determined by inverse gas chromatography. The study shows that polyethylene terephthalate-polyethylene naphthalate (PET-PEN) block-co-polyesters of defined sequence lengths can be prepared. Furthermore, the specific and dispersive surface energies of the obtained block-co-polyesters showed a linear dependence on the oligomer molecular weight and it was possible to regulate and control their interfacial properties. In contrast, with the corresponding random-block-co-polyesters no such dependence was found. The synthesized block-co-polyesters could be used as polymeric modifying agents for stabilizing PET-PEN polymer blends.
Poly(dimethylsiloxane) can be covalently coated with ultrathin NCO-sP(EO-stat-PO) hydrogel layers which permit covalent binding of cell adhesive moieties, while minimizing unspecific cell adhesion on non-functionalized areas. We applied long term uniaxial cyclic tensile strain (CTS) and revealed (a) the preservation of protein and cell-repellent properties of the NCO-sP(EO-stat-PO) coating and (b) the stability and bioactivity of a covalently bound fibronectin (FN) line pattern. We studied the adhesion of human dermal fibroblast (HDFs) on non-modified NCO-sP(EO-stat-PO) coatings and on the FN. HDFs adhered to FN and oriented their cell bodies and actin fibers along the FN lines independently of the direction of CTS. This mechanical long term stability of the bioactive, patterned surface allows unraveling biomechanical stimuli for cellular signaling and behavior to understand physiological and pathological cell phenomenon. Additionally, it allows for the application in wound healing assays, tissue engineering, and implant development demanding spatial control over specific cell adhesion.
Plasma polymerization is used for the modification and control of surface properties of a highly transparent, thermoplastic elastomeric silicone copolymer, GENIOMER® 80 (G80). PEG-like diglyme plasma polymer films were deposited with ether retentions varying between 20% and 70% as measured by X-ray photoelectron spectroscopy analysis which did not affect the transparency of the substrate. Films with ether retentions of greater than 70% inhibit protein binding (bovine serum albumin and fibrinogen) and cell proliferation. A short oxygen plasma pretreatment enhances the adhesion and stability of the film as shown by protein binding and cell adhesion experiments. The transparency of the material and the stability of the coating makes this material a versatile bulk material for technical (e.g., lab-on-a-chip) and biomedical (e.g., intraocular lens) applications. The G80/plasma polymer composite is stable against vigorous washing and storage over 5 months and, therefore, offers an attractive alternative to poly(dimethylsiloxane).
Melamine formaldehyde (MF) resins are widely used for the gluing and surface coating of wood-based consumer products in the interior design of living environments. MF resins are especially relevant in decorative laminate applications because of their good performance-to-price ratio. In their industrial processing, an important intermediate state is the liquid MF prepolymer that is used for decorative paper impregnation. Here, the drying of impregnated papers is investigated with respect to premature curing. A new method to quantify water release upon drying that allows estimation of the degree of undesired precuring is described. Since curing proceeds via polycondensation, crosslinking brings about the release of water molecules. By thermogravimetric analysis (TGA), drying was studied in terms of water release due to physical drying (elimination of “dilution water”) and chemical crosslinking of the prepolymer to a three-dimensional MF network (elimination of chemically liberated water). The results obtained by TGA/IR spectroscopic analysis of the liberated volatiles show that the emission of water from b-stage MF can be clearly analytically separated into a physical (evaporation of dilution water) and a chemical (liberation via condensation) sequence. TGA experiments were correlated with curing experiments performed with differential scanning calorimetry (DSC) to estimate the residual crosslinking capacities of the impregnated papers. The drying conditions used during the preparation of impregnated decorative papers seemed to significantly affect their remaining reactivity only when harsh drying conditions were used. Upon heat exposure for prolonged time, precuring of the oligomer units results in a shift of the temperature maxima in TGA.
Die Diskussion um Nachhaltigkeit und Ressourcenschonung hat die gesamte Industrie erreicht. Das Interesse an Naturfasern und Recyclingmaterialien ist gestiegen. An der Fakultät Textil und Design der Hochschule Reutlingen befasst sich die Forschungsgruppe Textile Verfahrenstechnik und Produktentwicklung in enger Kooperation mit mittelständischen Unternehmen mit Naturfasern und Recyclingmaterialien.
Positively charged metallic oxides prevent blood coagulation whereas negatively charged metallic oxides are thrombogenic. This study was performed to examine whether this effect extends to metallic oxide nanoparticles. Oscillation shear rheometry was used to study the effect of zinc oxide and silicon dioxide nanoparticles on thrombus formation in human whole blood. Our data show that oscillation shear rheometry is a sensitive and robust technique to analyze thrombogenicity induced by nanoparticles. Blood without previous contact with nanoparticles had a clotting time (CT) of 16.7 ± 1.0 min reaching a maximal clot strength (CS) of 16 ± 14 Pa (G') after 30 min. ZnO nanoparticles (diameter 70 nm, +37 mV zeta-potential) at a concentration of 1 mg/mL prolonged CT to 20.8 ± 3.6 min and provoked a weak clot (CS 1.5 ± 1.0 Pa). However, at a lower concentration of 100 µg/mL the ZnO particles dramatically reduced CT to 6.0 ± 0.5 min and increased CS to 171 ± 63 Pa. This procoagulant effect decreased at lower concentrations reaching the detection limit at 10 ng/mL. SiO2 nanoparticles (diameter 232 nm, −28 mV zeta-potential) at high concentrations (1 mg/mL) reduced CT (2.1 ± 0.2 min) and stimulated CS (249 ± 59 Pa). Similar to ZnO particles, this procoagulant effect reached a detection limit at 10 ng/mL. Nanoparticles in high concentrations reproduce the surface charge effects on blood coagulation previously observed with large particles or solid metal oxides. However, nanoparticles with different surface charges equally well stimulate coagulation at lower concentrations. This stimulation may be an effect which is not directly related to the surface charge.