In thermopervaporation the same economically favorable driving force as in membrane distillation, i.e., a temperature difference between feed and permeate for the transport, is used but with non-porous thin-film composite membranes. Membrane pores cannot be wetted and long-term operational stability can be achieved with the appropriate coating layer, but normally with a decrease of the flux compared to membrane distillation with porous hydrophobic membranes.
Porous asymmetric PVDF membranes were made to achieve low permeation resistance and pores which could be overcoated with polyelectrolyte polymers. This coating prohibits pore wetting and strongly reduces adsorption of organic substances.
Those membranes showed a high permeation rate for water due to a structure of phase-separated hydrophilic and hydrophobic three-dimensional domains. The permeation rates of these composite membranes for water is between 6 and 12 l/(h m²) at a feed temperature of 60 °C and permeate at a temperature of 40 °C of a 2% saline solution feed depending on the operational parameters. This is only a slight reduction of 10–15% in permeation rate compared to membrane distillation with porous hydrophobic membranes.
In whey dewatering experiment this membrane showed a constant performance over 4 days in intermittent operation mode and stability in cleaning with strong alkaline solution.
A vapor permeation processes for the separation of aromatic compounds from aliphatic compounds
(2014)
A number of rubbery and glassy membranes have been prepared and evaluated in vapor permeation experiments for separation of aromatic/aliphatic mixtures, using 5/95 (wt:wt) toluene/methylcyclohexane (MCH) as a model solution. Candidate membranes that met the required toluene/MCH selectivity of ≥ 10 were identified. The stability of the candidate membranes was tested by cycling the experiment between higher toluene concentrations and the original 5 wt% level. The best membrane produced has a toluene permeance of 280 gpu and a toluene/MCH selectivity of 13 when tested with a vapor feed of the model mixture at its boiling point and at atmospheric pressure. When a series of related membrane materials are compared, there is a sharp trade-off between membrane permeance and membrane selectivity. A process design study based on the experimental results was conducted. The best preliminary membrane design uses 45% of the energy of a conventional distillation process.