Refine
Year of publication
- 2023 (2) (remove)
Document Type
- Journal article (2)
Language
- English (2)
Is part of the Bibliography
- yes (2)
Institute
- Life Sciences (2)
Publisher
- American Chemical Society (1)
- Elsevier (1)
Film formation of self synthesized Polymer EPM–g–VTMDS (ethylene–propylene rubber, EPM, grafted with vinyltetramethyldisiloxane, VTMDS) was studied regarding bonding to adhesion promoter vinyltrimethoxysilane (VTMS) on oxidized 18/10 chromium/nickel–steel (V2A) stainless steel surfaces. Polymer films of different mixed solutions including commercial siloxane and silicone, dimethyl, vinyl group terminated crosslinker (HANSA SFA 42100, CAS# 68083-19-2, 0.35 mmol Vinyl/g) and platinum, 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complex Karstedt's catalyst (ALPA–KAT 1, CAS# 68478-92-2) were spin coated on V2A stainless steel surfaces with adsorbed VTMS thin layers in order to analyze film formation of EPM–g–VTMDS at early stages. Surface topography and chemical bonding of the high performance polymers on different oxidized V2A surfaces were investigated with X–ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and surface enhanced Raman spectroscopy (SERS). AFM and SEM as well as XPS results indicated that the formation of the polymer film proceeds via growth of polymer islands. Chemical signatures of the essential polymer contributions, linker and polymer backbones, could be identified using XPS core level peak shape analysis and also SERS. The appearance of signals which are related to Si–O–Si can be seen as a clear indication of lateral crosslinking and silica network formation in the films on the V2A surface.
Polyurethane thermosets have a wide range of applications. In this study, alternative raw materials were used to enhance sustainability. In two newly developed biobased polyurethanes (PUs), the cross-linker content was varied, which caused phase separation and therefore affected the turbidity. To investigate this phenomenon, UV–Vis–NIR spectroscopy was utilized. Spectra were recorded from 200 to 2500 nm in transmittance mode, and multivariate data analysis was applied to the three UV, Vis, and NIR sections separately. For the two different PU classes, each with five different cross-linker contents, classification by principal component analysis combined with linear or quadratic discriminant analysis was possible with an accuracy between 93% and nearly 100%. The best separation was achieved in the NIR range. Partial least-squares regression models were determined to predict the cross-linker content. As mentioned, the model for the NIR range is the most suitable, with the highest R2 (validation) of 0.99 for PU1 and 0.98 for PU2. The corresponding root-mean-square error of prediction values of the external validation was the lowest, with 0.82% (PU1) and 1.25% (PU2). Therefore, UV–Vis–NIR absorbance spectroscopy, especially NIR, is a suitable tool for monitoring the appropriate material composition of turbid PU thermosets in line.