Decorative laminates based on melamine formaldehyde (MF) resin impregnated papers are used at great extent for surface finishing of engineered wood that is used for furniture, kitchen, and working surfaces, flooring and exterior cladding. In all these applications, optically flawless appearance is a major issue. The work described here is focused on enhancing the cleanability and antifingerprint properties of smooth, matt surface-finished melamine-coated particleboards for furniture fronts, without at the same time changing or deteriorating other important surface parameters such as hardness, roughness or gloss. In order to adjust the surface polarity of a low pressure melamine film, novel interface-active macromolecular compounds were prepared and tested for their suitability as an antifingerprint additive. Two hydroxy-functional surfactants (polydimethysiloxane, PDMS-OH and perfluoroether, PF-OH) were oxidized under mild conditions to the corresponding aldehydes (PDMS-CHO and PF-CHO) using a pyridinium chlorochromate catalyst. With the most promising oxidized polymeric additive, PDMS-CHO, the contact angles against water, n-hexadecane, and squalene increased from 79.8°, 26.3° and 31.4° for the pure MF surface to 108.5°, 54.8°, and 59.3°, respectively, for the modified MF surfaces. While for the laminated MF surface based on the oxidized fluoroether the gloss values were much higher than required, for the surfaces based on oxidized polydimethylsiloxane the technological values as well as the lower gloss values were in agreement with the requirements and showed much improved surface cleanability, as was also confirmed by colorimetric measurements.
Melamine-formaldehyde (MF) resins are widely used as surface finishes for engineered wood-based panels in decorative laminates. Since no additional glue is applied in lamination, the overall residual curing capacity of MF resins is of great technological importance. Residual curing capacity is measured by differential scanning calorimetry (DSC) as the exothermic curing enthalpy integral of the liquid resin. After resin synthesis is completed, the resulting pre-polymer has a defined chemical structure with a corresponding residual curing capacity. Predicting the residual curing capacity of a resin batch already at an early stage during synthesis would enable corrective measures to be taken by making adjustments while synthesis is still in progress. Thereby, discarding faulty batches could be avoided. Here, by using a batch modelling approach, it is demonstrated how quantitative predictions of MF residual curing capacity can be derived from inline Fourier Transform infrared (FTIR) spectra recorded during resin synthesis using partial least squares regression. Not only is there a strong correlation (R2 = 0.89) between the infrared spectra measured at the end of MF resin synthesis and the residual curing capacity. The inline reaction spectra obtained already at the point of complete dissolution of melamine upon methylolation during the initial stage of resin synthesis are also well suited for predicting final curing performance of the resin. Based on these IR spectra, a valid regression model (R2 = 0.85) can be established using information obtained at a very early stage of MF resin synthesis.
Melamine-formaldehyde resins are widely used for decorative paper impregnation. Resin properties relevant for impregnation are mainly determined already at the stage of resin synthesis by the applied reaction conditions. Thus, understanding the relationship between reaction conditions and technological properties is important. Response surface methodology based on orthogonal parameter level variations is the most suitable tool to identify and quantify factor effects and deduce causal correlation patterns. Here, two major process factors of MF resin synthesis were systematically varied using such a statistical experimental design. To arrive at resins having a broad range of technological properties, initial pH and M:F ratio were varied in a wide range (pH: 7.9–12.1; M:F ratio: 1:1.5–1:4.5). The impregnation behavior of the resins was modeled using viscosity, penetration rate and residual curing capacity as technological responses. Based on the response surface models, nonlinear and synergistic action of process factors was quantified and a suitable process window for preparing resins with favorable impregnation performance was defined. It was found that low M:F ratios (~1:2–1:2.5) and comparatively high starting pHs (~pH 11) yield impregnation resins with rapid impregnation behavior and good residual curing capacity.
Mass-customization is a megatrend that also affects the wood industry. To obtain individually designed laminates in batch size one efficient printing and processing technologies are required. Digital printing was envisaged as it does not depend on highly costly printing cylinders (as used in rotogravure printing) and allows rapid exchange of the printing designs. In the present work, two wellestablished digital printing approaches, the multi-pass and the single-pass technique, were investigated and evaluated for their applicability in decorating engineered wood and low-pressure melamine films. Three different possibilities of implementing digital printing in the decorative laminates manufacturing process were studied: (1) digital printing on coated chipboard and subsequently applying a lacquered top-coat or melamine overlay (designated as “direct printing”, since the LPM was the printing substrate), (2) digital printing on decorative paper which was subsequently impregnated before hot pressing (designated as “indirect printing, variant A”) and (3) digital printing on decorative paper with subsequent interlamination of the paper between impregnated under- and overlay paper layers during the pressing process (designated as “indirect printing, variant B”). Due to various advantages of the resulting cured melamine resin surfaces including a much better technological performance and flexibility in surface texture design, it was decided to industrially further pursue only the indirect digital printing process comprising interlamination and the direct printing process with a melamine overlay-finishing. Basis for the successful trials on production and laboratory scales were the identification of applicable inks (in terms of compatibility with melamine resin) and of appropriate printing paper quality (in terms of impregnation and imprinting ability). After selection and fine tuning of suitable materials, the next challenge to overcome was the initially insufficient bond strength between impregnated overlay and the ink layers which led to unsatisfactory quality of the print appearance and delamination effects. However, the optimization of the pressing program and the development of a modified impregnation procedure for the underlay and overlay papers allowed the successful implementation of digital printing in the production line of our industrial partner FunderMax.
Properties data of phenolic resins synthetized for the impregnation of saturating Kraft paper
(2018)
The quality of decorative laminates boards depends on the impregnation process of Kraft papers with a phenolic resin,which constitute the raw materials for the manufacture of the cores of such boards.In the laminates industries,the properties of resins are adapted via their syntheses,usually by mixing phenol and formaldehyde in a batch,where additives,temperature and stirring parameters can be controlled. Therefore, many possibilities of preparation and phenolic resins exist, that leads to different combinations of physico chemical properties. In this article, the properties data of eight phenolic resins synthetized with different parameters of pH and reaction times at 60 °C and 90 °C are presented: the losses of pH after synthesis and the dynamic viscosities measured after synthesis and one the solid content is adjusted to 45%w/w in methanol. Data aquired by Differential Scanning Calorimetry (DSC) of the resins and Inverse Gas Chromatography (IGC) of cured solids are given as well.
High quality decorative laminate panels typically consist of two major types of components: the surface layers comprising décor and overlay papers that are impregnated with melamine-based resins, and the core which is made of stacks of kraft papers impregnated with phenolic (PF) resin. The PF-impregnated layers impart superior hydrolytic stability, mechanical strength and fire-resistance to the composite. The manufacturing involves the complex interplay between resin, paper and impregnation/drying processes. Changes in the input variables cause significant alterations in the process characteristics and adaptations of the used materials and specific process conditions may, in turn, be required. This review summarizes the main variables influencing both processability and technological properties of phenolic resin impregnated papers and laminates produced therefrom. It is aimed at presenting the main influences from the involved components (resin and paper), how these may be controlled during the respective process steps (resin preparation and paper production), how they influence the impregnation and lamination conditions, how they affect specific aspects of paper and laminate performance, and how they interact with each other
(synergies).
Impact of phenolic resin preparation on its properties and its penetration behavior in Kraft paper
(2018)
The core of decorative laminates is generally made of stacked Kraft paper sheets impregnated with a phenolic resin. As the impregnation process in industry is relatively fast, new methods need to be developed to characterize it for different paper-resin systems. Several phenolic resins were synthesized with the same Phenol:Formaldehyde ratio of 1:1.8 and characterized by Fourier Transform Infrared Spectrometry (FTIR) as well as Size-Exclusion Chromatography (SEC). In addition, their viscosities and surface tensions when diluted in methanol to 45% of solid content were measured. The capacity of each resin to penetrate a Kraft paper sheet was characterized using a new method, which measures the conductivities induced by the liquid resin crossing the paper substrate. With this method, crossing times could be measured with a good accuracy. Surprisingly, the results showed that the penetration time of the resin samples is not correlated to the viscosity values, but rather to the surface tension characteristics and the chemical characteristics of paper. Furthermore, some resins had a higher swelling effect on the fibers that delayed the crossing of the liquid through the paper.
Here, the effects of substituting portions of fossil-based phenol in phenol formaldehyde resin by renewable lignin from two different sources are investigated using a factorial screening experimental design. Among the resins consumed by the wood-based industry, phenolics are one of the most important types used for impregnation, coating or gluing purposes. They are prepared by condensing phenol with formaldehyde (PF). One major use of PF is as matrix polymer for decorative laminates in exterior cladding and wet-room applications. Important requirements for such PFs are favorable flow properties (low viscosity), rapid curing behavior (high reactivity) and sufficient self-adhesion capacity (high residual curing potential). Partially substituting phenol in PF with bio-based phenolic co-reagents like lignin modifies the physicochemical properties of the resulting resin. In this study, phenol-formaldehyde formulations were synthesized where either 30% or 50% (in weight) of the phenol monomer were substituted by either sodium lignosulfonate or Kraft lignin. The effect of modifying the lignin material by phenolation before incorporation into the resin synthesis was also investigated. The resins so obtained were characterized by Fourier Transform Infra-Red (FTIR) spectroscopy, Size Exclusion Chromatography (SEC), Differential Scanning Calorimetry (DSC), rheology, and measurements of contact angle and surface tension using the Wilhelmy plate method and drop shape analysis.
Impregnated paper-based decorative laminates prepared from lignin-substituted phenolic resins
(2020)
High Pressure Laminates (HPL) panels consist of stacks of self-gluing paper sheets soaked with phenol-formaldehyde (PF) resins. An important requirement for such PFs is that they must rapidly penetrate and saturate the paper pores. Partially substituting phenol with bio-based phenolic chemicals like lignin changes the physico-chemical properties of the resin and affects its ability to penetrate the paper. In this study, PF formulations containing different proportions of lignosulfonate and kraft lignin were used to prepare paper-based laminates. The penetration of a Kraft paper sheet was characterized by a recently introduced, new device measuring the conductivity between both sides of the paper sheet after a drop of resin was placed on the surface and allowed to penetrate the sheet. The main target value measured was the time required for a specific resin to completely penetrate the defined paper sample (“penetration time”). This penetration time generally depends on the molecular weight distribution, the flow behavior and the polarity of the resin which in turn are dependent on the manufacturing conditions of the resin. In the present study, the influences of the three process factors: (1) type of lignin material used for substitution, (2) lignin modification by phenolation and (3) degree of phenol substitution on the penetration times of various lignin-phenolic hybrid impregnation resins were studied using a complete twolevel three-factorial experimental design. Thin laminates made with the resins diluted in methanol were mechanically tested in terms of tensile and flexural strains, and their cross-sections were studied by light microscopy.
This article provides a general overview of the most promising candidates of bio based materials and deals with the most important issues when it comes to their incorporation into PF resins. Due to their abundance on Earth, much knowledge of lignin-based materials has already been gained and uses of lignin in PF resins have been studied for many decades. Other natural polyphenols that are less frequently considered for impregnation are covered as well, as they do also possess some potential for PF substitution.