Melamine formaldehyde (MF) resins are widely used for the gluing and surface coating of wood-based consumer products in the interior design of living environments. MF resins are especially relevant in decorative laminate applications because of their good performance-to-price ratio. In their industrial processing, an important intermediate state is the liquid MF prepolymer that is used for decorative paper impregnation. Here, the drying of impregnated papers is investigated with respect to premature curing. A new method to quantify water release upon drying that allows estimation of the degree of undesired precuring is described. Since curing proceeds via polycondensation, crosslinking brings about the release of water molecules. By thermogravimetric analysis (TGA), drying was studied in terms of water release due to physical drying (elimination of “dilution water”) and chemical crosslinking of the prepolymer to a three-dimensional MF network (elimination of chemically liberated water). The results obtained by TGA/IR spectroscopic analysis of the liberated volatiles show that the emission of water from b-stage MF can be clearly analytically separated into a physical (evaporation of dilution water) and a chemical (liberation via condensation) sequence. TGA experiments were correlated with curing experiments performed with differential scanning calorimetry (DSC) to estimate the residual crosslinking capacities of the impregnated papers. The drying conditions used during the preparation of impregnated decorative papers seemed to significantly affect their remaining reactivity only when harsh drying conditions were used. Upon heat exposure for prolonged time, precuring of the oligomer units results in a shift of the temperature maxima in TGA.
Decorative laminates based on melamine formaldehyde (MF) resin impregnated papers are used at great extent for surface finishing of engineered wood that is used for furniture, kitchen, and working surfaces, flooring and exterior cladding. In all these applications, optically flawless appearance is a major issue. The work described here is focused on enhancing the cleanability and antifingerprint properties of smooth, matt surface-finished melamine-coated particleboards for furniture fronts, without at the same time changing or deteriorating other important surface parameters such as hardness, roughness or gloss. In order to adjust the surface polarity of a low pressure melamine film, novel interface-active macromolecular compounds were prepared and tested for their suitability as an antifingerprint additive. Two hydroxy-functional surfactants (polydimethysiloxane, PDMS-OH and perfluoroether, PF-OH) were oxidized under mild conditions to the corresponding aldehydes (PDMS-CHO and PF-CHO) using a pyridinium chlorochromate catalyst. With the most promising oxidized polymeric additive, PDMS-CHO, the contact angles against water, n-hexadecane, and squalene increased from 79.8°, 26.3° and 31.4° for the pure MF surface to 108.5°, 54.8°, and 59.3°, respectively, for the modified MF surfaces. While for the laminated MF surface based on the oxidized fluoroether the gloss values were much higher than required, for the surfaces based on oxidized polydimethylsiloxane the technological values as well as the lower gloss values were in agreement with the requirements and showed much improved surface cleanability, as was also confirmed by colorimetric measurements.