Polyurethane thermosets have a wide range of applications. In this study, alternative raw materials were used to enhance sustainability. In two newly developed biobased polyurethanes (PUs), the cross-linker content was varied, which caused phase separation and therefore affected the turbidity. To investigate this phenomenon, UV–Vis–NIR spectroscopy was utilized. Spectra were recorded from 200 to 2500 nm in transmittance mode, and multivariate data analysis was applied to the three UV, Vis, and NIR sections separately. For the two different PU classes, each with five different cross-linker contents, classification by principal component analysis combined with linear or quadratic discriminant analysis was possible with an accuracy between 93% and nearly 100%. The best separation was achieved in the NIR range. Partial least-squares regression models were determined to predict the cross-linker content. As mentioned, the model for the NIR range is the most suitable, with the highest R2 (validation) of 0.99 for PU1 and 0.98 for PU2. The corresponding root-mean-square error of prediction values of the external validation was the lowest, with 0.82% (PU1) and 1.25% (PU2). Therefore, UV–Vis–NIR absorbance spectroscopy, especially NIR, is a suitable tool for monitoring the appropriate material composition of turbid PU thermosets in line.
This study introduces a straightforward approach to construct three-dimensional (3D) surface-enhanced Raman spectroscopy (SERS) substrates using chemically modified silica particles as microcarriers and by attaching metal nanoparticles (NPs) onto their surfaces. Tollens’ reagent and sputtering techniques are utilized to prepare the SERS substrates from mercapto-functionalized silica particles. Treatment with Tollens’ reagent generates a variety of silver NPs, ranging from approximately 10 to 400 nm, while sputtering with gold (Au) yields uniformly distributed NPs with an island-like morphology. Both substrates display wide plasmon resonances in the scattering spectra, making them effective for SERS in the visible spectral range, with enhancement factors (ratio of the analyte’s intensity at the hotspot compared to that on the substrate in the absence of metal nanoparticles) of up to 25. These 3D substrates have a significant advantage over traditional SERS substrates because their active surface area is not limited to a 2D surface but offers a much greater active surface due to the 3D arrangement of the NPs. This feature may enable achieving much higher SERS intensity from within streaming liquids or inside cells/tissues.