The hard template method for the preparation of monodisperse mesoporous silica microspheres (MPSMs) has been established in recent years. In this process, in situ-generated silica nanoparticles (SNPs) enter the porous organic template and control the size and pore parameters of the final MPSMs. Here, the sizes of the deposited SNPs are determined by the hydrolysis and condensation rates of different alkoxysilanes in a base catalyzed sol–gel process. Thus, tetramethyl orthosilicate (TMOS), tetraethyl orthosilicate (TEOS), tetrapropyl orthosilicate (TPOS) and tetrabutyl orthosilicate (TBOS) were sol–gel processed in the presence of amino-functionalized poly (glycidyl methacrylate-co-ethylene glycol dimethacrylate) (p(GMA-co-EDMA)) templates. The size of the final MPSMs covers a broad range of 0.5–7.3 µm and a median pore size distribution from 4.0 to 24.9 nm. Moreover, the specific surface area can be adjusted between 271 and 637 m2 g−1. Also, the properties and morphology of the MPSMs differ according to the SNPs. Furthermore, the combination of different alkoxysilanes allows the individual design of the morphology and pore parameters of the silica particles. Selected MPSMs were packed into columns and successfully applied as stationary phases in high-performance liquid chromatography (HPLC) in the separation of various water-soluble vitamins.
Hybrid organic/inorganic nanocomposites combine the distinct properties of the organic polymer and the inorganic filler, resulting in overall improved system properties. Monodisperse porous hybrid beads consisting of tetraethylene pentamine functionalized poly(glycidyl methacrylateco-ethylene glycol dimethacrylate) particles and silica nanoparticles (SNPs) were synthesized under Stoeber sol-gel process conditions. A wide range of hybrid organic/silica nanocomposite materials with different material properties was generated. The effects of n(H2O)/n(TEOS) and c(NH3 ) on the hybrid bead properties particle size, SiO2 content, median pore size, specific surface area, pore volume and size of the SNPs were studied. Quantitative models with a high robustness and predictive power were established using a statistical and systematic approach based on response surface methodology. It was shown that the material properties depend in a complex way on the process factor settings and exhibit non-linear behaviors as well as partly synergistic interactions between the process factors. Thus, the silica content, median pore size, specific surface area, pore volume and size of the SNPs are non-linearly dependent on the water-to-precursor ratio. This is attributed to the effect of the water-to-precursor ratio on the hydrolysis and condensation rates of TEOS. A possible mechanism of SNP incorporation into the porous polymer network is discussed.
The data presented in this article characterize the thermomechanical and microhardness properties of a novel melamine-formaldehyde resin (MF) intended for the use as a self-healing surface coating. The investigated MF resin is able to undergo reversible crosslinking via Diels Alder reactive groups. The microhardness data were obtained from nanoindentation measurements performed on solid resin film samples at different stages of the self-healing cycle. Thermomechanical analysis was performed under dynamic load conditions. The data provide supplemental material to the manuscript published by Urdl et al. 2020 (https://doi.org/10.1016/j.eurpolymj.2020.109601) on the self-healing performance of this resin, where a more thorough discussion on the preparation, the properties of this coating material and its application in impregnated paper-based decorative laminates can be found.
Vitamin E (VitE) additives are important in treating osteoarthritis inclusive cartilage regeneration due to their antioxidant and anti-inflammatory properties. The present research study focuses on the ability of biological antioxidant VitE (alpha-tocopherol isoform) to reduce or minimize oxidative degradation of soft implantable polyurethane (PU) elastomers after extended periods of time (5 months) in vitro. The effect of the oxidation storage media on the morphology of the segmented PUs was evaluated by mechanical softening, crystallization and melting behavior of both soft and hard segments (SS, HS) using dynamic mechanical analysis (DMA). Bulk mechanical properties of the potential implant materials during ageing were predicted from comprehensive mechanical testing of the biomaterials under tension and compression cyclic loads. 5-months in vitro data suggest that the prepared siloxane-poly(carbonate urethane) formulations have sufficient resistance against degradation to be suitable materials for chondral long term bio-stable implants. Most importantly, the positive effect of incorporating VitE (0.5 or 1.0% w/w) as bio-antioxidant and lubricant on the bio-stability was observed for all PU types. VitE-additives protected the surface layer from erosion and cracking during chemical oxidation in vitro as well as from thermal oxidation during extrusion re-processing.
The data present in this article affords insides in the characterization of a newly described bi-functional furan-melamine monomer, which is used for the production of monodisperse, furan-functionalized melamine formaldehyde particles. In the related research article Urdl et al., 2019 data interpretations can be found. The furan functionalization of particles is necessary to perform reversible Diels-Alder reactions with maleimide (BMI) crosslinker to form thermoreversible network systems. To understand the reaction conditions of Diels Alder (DA) reaction with a Fu-Mel monomer and a maleimide crosslinker, model DA reaction were performed and evaluated using dynamic FT-IR measurements. During retro Diels-Alder (rDA) reactions of the monomer system, it was found out that some side reaction occurred at elevated temperatures. The data of evaluating the side reaction is described in one part of this manuscript. Additional high resolution SEM images of Fu Mel particles are shown and thermoreversible particle networks with BMI2 are shown. The data of different Fu-Mel particle networks with maleimide crosslinker are presented. Therefore, the used maleimide crosslinker with different spacer lengths were synthesized and the resulting networks were analyzed by ATR-FT-IR, SEM and DSC.
Properties data of phenolic resins synthetized for the impregnation of saturating Kraft paper
(2018)
The quality of decorative laminates boards depends on the impregnation process of Kraft papers with a phenolic resin,which constitute the raw materials for the manufacture of the cores of such boards.In the laminates industries,the properties of resins are adapted via their syntheses,usually by mixing phenol and formaldehyde in a batch,where additives,temperature and stirring parameters can be controlled. Therefore, many possibilities of preparation and phenolic resins exist, that leads to different combinations of physico chemical properties. In this article, the properties data of eight phenolic resins synthetized with different parameters of pH and reaction times at 60 °C and 90 °C are presented: the losses of pH after synthesis and the dynamic viscosities measured after synthesis and one the solid content is adjusted to 45%w/w in methanol. Data aquired by Differential Scanning Calorimetry (DSC) of the resins and Inverse Gas Chromatography (IGC) of cured solids are given as well.
A series of novel biomedical TPCUs with different percentages of hard segment and a silicone component in the soft segment were synthesized in a multi stage one-pot method. The kinetic profiles of the urethane formation in TPCU-based copolymer systems were monitored by rheological, in line FTIR spectroscopic (React IR) and real-time calorimetric (RC1) methods. This process-analytically monitored multi step synthesis was successfully used to optimize the production of medical-grade TPCU elastomers on preparative scale (in lots of several kg) with controlled molecular structure and mechanical properties. Various surface and bulk analytical methods as well as systematic studies of the mechanic response of the elastomer end-products towards compression and tensile loading were used to estimate the bio-stability of the prepared TPCUs in vitro after 3 months. The tests suggested that high bio-stability of all polyurethane formulations using accelerating in vitro test can be attributed to the synthetic design as well as to the specific techniques used for specimen preparation, namely: (1) the annealing for reducing residual polymer surface stress and preventing IES, (2) stabilization of the morphology by long time storage of the specimens after processing before being immersed in the test liquids, (3) purification by extraction to remove the shot chain oligomers which are the most susceptible to degradation. All mechanical tests were performed on cylindrical and circular disc specimens for modelling the thickness of the meniscus implants under application-relevant stress conditions.
This article contains data on the synthesis and mechanical characterization of polysiloxane-based urea-elastomers (PSUs) and is related to the research article entitled “Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application” (Riehle et al., 2018) [1]. These elastomers were prepared by a two-step polyaddition using the aliphatic diisocyanate 4,4′-Methylenbis(cyclohexylisocyanate) (H12MDI), a siloxane-based chain extender 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (APTMDS) and amino-terminated polydimethylsiloxanes (PDMS) or polydimethyl-methyl-phenyl-siloxane-copolymers (PDMS-Me,Ph), respectively. (More details about the synthesis procedure and the reaction scheme can be found in the related research article (Riehle et al., 2018) [1]).
Amino-terminated polydimethylsiloxanes with varying molecular weights and PDMS-Me,Ph-copolymers were prepared prior by a base-catalyzed ring-chain equilibration of a cyclic siloxane and the endblocker APTMDS. This DiB article contains a procedure for the synthesis of the base catalyst tetramethylammonium-3-aminopropyl-dimethylsilanolate and a generic synthesis procedure for the preparation of a PDMS having a targeted number average molecular weight of 3000 g mol−1. Molecular weights and the amount of methyl-phenyl-siloxane within the polysiloxane-copolymers were determined by 1H NMR and 29Si NMR spectroscopy. The corresponding NMR spectra and data are described in this article.
Additionally, this DiB article contains processed data on in line and off line FTIR-ATR spectroscopy, which was used to follow the reaction progress of the polyaddition by showing the conversion of the diisocyanate. All relevant IR band assignments of a polydimethylsiloxane-urea spectrum are described in this article.
Finally, data on the tensile properties and the mechanical hysteresis-behaviour at 100% elongation of PDMS-based polyurea-elastomers are shown in dependence to the PDMS molecular weight.