Refine
Document Type
- Journal article (60)
- Book chapter (15)
- Conference proceeding (4)
- Book (2)
- Review (1)
Is part of the Bibliography
- yes (82)
Institute
- Life Sciences (81)
- Technik (1)
Publisher
- Elsevier (35)
- MDPI (12)
- Wiley (10)
- American Chemical Society (4)
- Tech Science Press (4)
- Springer (3)
- De Gruyter (2)
- Taylor & Francis (2)
- CRC Press (1)
- Institut für Holztechnologie (1)
- JoVE (1)
- Shaker Verlag (1)
- Technical Conference Management (1)
- University of Technology and Economics (1)
Vitamin E (VitE) additives are important in treating osteoarthritis inclusive cartilage regeneration due to their antioxidant and anti-inflammatory properties. The present research study focuses on the ability of biological antioxidant VitE (alpha-tocopherol isoform) to reduce or minimize oxidative degradation of soft implantable polyurethane (PU) elastomers after extended periods of time (5 months) in vitro. The effect of the oxidation storage media on the morphology of the segmented PUs was evaluated by mechanical softening, crystallization and melting behavior of both soft and hard segments (SS, HS) using dynamic mechanical analysis (DMA). Bulk mechanical properties of the potential implant materials during ageing were predicted from comprehensive mechanical testing of the biomaterials under tension and compression cyclic loads. 5-months in vitro data suggest that the prepared siloxane-poly(carbonate urethane) formulations have sufficient resistance against degradation to be suitable materials for chondral long term bio-stable implants. Most importantly, the positive effect of incorporating VitE (0.5 or 1.0% w/w) as bio-antioxidant and lubricant on the bio-stability was observed for all PU types. VitE-additives protected the surface layer from erosion and cracking during chemical oxidation in vitro as well as from thermal oxidation during extrusion re-processing.
Homogeneous and monodispersed furan functionalised melamine-formaldehyde particles were produced. As a precursor, 2-chloro-1,3,5-triazine-2,4-diamine (Mel) was selectively substituted with 2-aminomethyl furan (Fu) units in a convenient one step reaction. The pure reaction product Fu-Mel, which was used without further purification, was reacted with formaldehyde by conventional sol-gel condensation in aqueous medium to yield chemically homogenous, spherically shaped and monodispersed particles. The particles were analysed using ATR-FT-IR, Raman, 1H and 13C NMR spectroscopy, TGA, SEM and DSC measurements. The reactivity of the furan groups located at the particle surface was studied by performing a thermoreversible Diels-Alder cycloaddition reaction with bis-maleimide coupling agents. The formed networks showed thermoreversible behaviour, which was characterised by dynamic IR and DSC measurements.
The data present in this article affords insides in the characterization of a newly described bi-functional furan-melamine monomer, which is used for the production of monodisperse, furan-functionalized melamine formaldehyde particles. In the related research article Urdl et al., 2019 data interpretations can be found. The furan functionalization of particles is necessary to perform reversible Diels-Alder reactions with maleimide (BMI) crosslinker to form thermoreversible network systems. To understand the reaction conditions of Diels Alder (DA) reaction with a Fu-Mel monomer and a maleimide crosslinker, model DA reaction were performed and evaluated using dynamic FT-IR measurements. During retro Diels-Alder (rDA) reactions of the monomer system, it was found out that some side reaction occurred at elevated temperatures. The data of evaluating the side reaction is described in one part of this manuscript. Additional high resolution SEM images of Fu Mel particles are shown and thermoreversible particle networks with BMI2 are shown. The data of different Fu-Mel particle networks with maleimide crosslinker are presented. Therefore, the used maleimide crosslinker with different spacer lengths were synthesized and the resulting networks were analyzed by ATR-FT-IR, SEM and DSC.
Melamine–formaldehyde (MF) resins are widely used as adhesives and finishing materials in the wood industry. During resin cure, either methylene ether or methylene bridges are formed, leading to the formation of a three‐dimensional resin network. Not only the curing degree, but also the chemical species present in the cured resin determine the quality of the final product. Analytical methods allowing a detailed investigation of network formation are of great benefit to manufacturers. In the present work, resin cure of an MF precondensate is studied at different temperatures (100–200 °C) without considering the initial pH as a factor. Isoconversional kinetic analysis based on exothermal curing enthalpies enables calculation of the crosslinking degree at a given time/temperature regime. A semiquantitative determination of the chemical groups present is performed based on solid‐state nuclear magnetic resonance data. Fourier transform infrared spectroscopy has shown to be a fast and reliable analytical tool with high sensitivity toward functional groups and with great potential for at‐line process control.
Impact of phenolic resin preparation on its properties and its penetration behavior in Kraft paper
(2018)
The core of decorative laminates is generally made of stacked Kraft paper sheets impregnated with a phenolic resin. As the impregnation process in industry is relatively fast, new methods need to be developed to characterize it for different paper-resin systems. Several phenolic resins were synthesized with the same Phenol:Formaldehyde ratio of 1:1.8 and characterized by Fourier Transform Infrared Spectrometry (FTIR) as well as Size-Exclusion Chromatography (SEC). In addition, their viscosities and surface tensions when diluted in methanol to 45% of solid content were measured. The capacity of each resin to penetrate a Kraft paper sheet was characterized using a new method, which measures the conductivities induced by the liquid resin crossing the paper substrate. With this method, crossing times could be measured with a good accuracy. Surprisingly, the results showed that the penetration time of the resin samples is not correlated to the viscosity values, but rather to the surface tension characteristics and the chemical characteristics of paper. Furthermore, some resins had a higher swelling effect on the fibers that delayed the crossing of the liquid through the paper.
Functionalised particles are highly requested in materials research, as they can be used as vital components in many advanced applications such as smart materials, functional coatings, drug carrier systems or adsorption materials. In this study, furan-functionalised melamine-formaldehyde (MF) particles were successfully prepared for the first time using an organic sol-gel process. Commercially available 2-Aminomethylfuran (AMF) and 2-Aminomethyl-5-methylfuran (AMMF) were used as modifying agents. In the isolated polymer particles, a melamine (M) to modifying agent ratio of M:AMF mol/mol 2.04:1 and M:AMMF ratio of mol/mol 1.25:1 was used. The obtained particles were isolated in various centrifugation and re-dispersion cycles and analysed using ATR-FT-IR, Raman and solid state 13C NMR spectroscopy, TGA, SEM and DSC measurements. Upon functionalisation the size of the MF particles increased (MF 1.59 µm, 27% CV (coefficient of variation); MF-AMF 2.56 µm, 25% CV; MF-AMMF 2.20 µm, 35% CV). DSC measurements showed that another type of exothermic residual reactivity besides condensation-based curing takes place with the furan-modified particles that is not related to the liberation of volatile compounds. The newly obtained particles are able to undergo Diels-Alder reactions with maleimide groups. The characteristic IR and Raman absorbance bands of the reaction products after the particles were reacted with 4,4′-Diphenylmethanebismaleimide reagent confirm the formation of a Diels-Alder adduct.
Properties data of phenolic resins synthetized for the impregnation of saturating Kraft paper
(2018)
The quality of decorative laminates boards depends on the impregnation process of Kraft papers with a phenolic resin,which constitute the raw materials for the manufacture of the cores of such boards.In the laminates industries,the properties of resins are adapted via their syntheses,usually by mixing phenol and formaldehyde in a batch,where additives,temperature and stirring parameters can be controlled. Therefore, many possibilities of preparation and phenolic resins exist, that leads to different combinations of physico chemical properties. In this article, the properties data of eight phenolic resins synthetized with different parameters of pH and reaction times at 60 °C and 90 °C are presented: the losses of pH after synthesis and the dynamic viscosities measured after synthesis and one the solid content is adjusted to 45%w/w in methanol. Data aquired by Differential Scanning Calorimetry (DSC) of the resins and Inverse Gas Chromatography (IGC) of cured solids are given as well.
A series of novel biomedical TPCUs with different percentages of hard segment and a silicone component in the soft segment were synthesized in a multi stage one-pot method. The kinetic profiles of the urethane formation in TPCU-based copolymer systems were monitored by rheological, in line FTIR spectroscopic (React IR) and real-time calorimetric (RC1) methods. This process-analytically monitored multi step synthesis was successfully used to optimize the production of medical-grade TPCU elastomers on preparative scale (in lots of several kg) with controlled molecular structure and mechanical properties. Various surface and bulk analytical methods as well as systematic studies of the mechanic response of the elastomer end-products towards compression and tensile loading were used to estimate the bio-stability of the prepared TPCUs in vitro after 3 months. The tests suggested that high bio-stability of all polyurethane formulations using accelerating in vitro test can be attributed to the synthetic design as well as to the specific techniques used for specimen preparation, namely: (1) the annealing for reducing residual polymer surface stress and preventing IES, (2) stabilization of the morphology by long time storage of the specimens after processing before being immersed in the test liquids, (3) purification by extraction to remove the shot chain oligomers which are the most susceptible to degradation. All mechanical tests were performed on cylindrical and circular disc specimens for modelling the thickness of the meniscus implants under application-relevant stress conditions.
Soft thermoplastic polysiloxane-urea-elastomers (PSUs) were prepared for the application as a biomaterial to replace the human natural lens after cataract surgery. PSUs were synthesized from amino-terminated polydimethylsiloxanes (PDMS), 4,4′-Methylenebis(cyclohexylisocyanate) (H12MDI) and 1,3–Bis(3-aminopropyl)-1,1,3,3–tetramethyldisiloxane (APTMDS) by a two-step polyaddition route. Such a material has to be highly transparent and must exhibit a low Young’s Modulus and excellent dimensional stability. Polydimethylsiloxanes in the range of 3000–33,000 g·mol−1 were therefore prepared by ring-chain-equilibration of octamethylcyclotetrasiloxane (D4) and APTMDS in order to study the influence of the soft segment molecular weight on the mechanical properties and the transparency of the PSU-elastomers. 2,4,6,8-Tetramethyl-2,4,6,8-tetraphenylcyclotetrasiloxane (D4Me,Ph) was co-polymerized with D4 in order to adjust the refractive index of the polydimethyl-methyl-phenyl-siloxane-copolymers to a value equivalent to a young human natural lens. Very elastic PSUs with Elongation at Break values higher than 700% were prepared. PSU-elastomers, synthesized from PDMS of molecular weights up to 18,000 g·mol−1, showed transmittance values of over 90% within the visible spectrum range. The soft segment refractive index was increased through the incorporation of 14 mol % of methyl-phenyl-siloxane from 1.4011 to 1.4346 (37 °C). Young’s Moduli of PSU-elastomers were around 1 MPa and lower at PDMS molecular weights up to 15,000 g·mol−1. 10-cycle hysteresis measurements were applied to evaluate the mechanical stability of the PSUs at repeated stress. Hysteresis values at 100% strain decreased from 32 to 2% (10th cycle) with increasing PDMS molecular weight. Furthermore, hysteresis at 5% strain was only detected in PSU-elastomers with low PDMS molecular weights. Finally, preliminary results of in vitro cytotoxicity tests on a PSU-elastomer showed no toxic effects on HaCaT-cells.
This article contains data on the synthesis and mechanical characterization of polysiloxane-based urea-elastomers (PSUs) and is related to the research article entitled “Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application” (Riehle et al., 2018) [1]. These elastomers were prepared by a two-step polyaddition using the aliphatic diisocyanate 4,4′-Methylenbis(cyclohexylisocyanate) (H12MDI), a siloxane-based chain extender 1,3-Bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (APTMDS) and amino-terminated polydimethylsiloxanes (PDMS) or polydimethyl-methyl-phenyl-siloxane-copolymers (PDMS-Me,Ph), respectively. (More details about the synthesis procedure and the reaction scheme can be found in the related research article (Riehle et al., 2018) [1]).
Amino-terminated polydimethylsiloxanes with varying molecular weights and PDMS-Me,Ph-copolymers were prepared prior by a base-catalyzed ring-chain equilibration of a cyclic siloxane and the endblocker APTMDS. This DiB article contains a procedure for the synthesis of the base catalyst tetramethylammonium-3-aminopropyl-dimethylsilanolate and a generic synthesis procedure for the preparation of a PDMS having a targeted number average molecular weight of 3000 g mol−1. Molecular weights and the amount of methyl-phenyl-siloxane within the polysiloxane-copolymers were determined by 1H NMR and 29Si NMR spectroscopy. The corresponding NMR spectra and data are described in this article.
Additionally, this DiB article contains processed data on in line and off line FTIR-ATR spectroscopy, which was used to follow the reaction progress of the polyaddition by showing the conversion of the diisocyanate. All relevant IR band assignments of a polydimethylsiloxane-urea spectrum are described in this article.
Finally, data on the tensile properties and the mechanical hysteresis-behaviour at 100% elongation of PDMS-based polyurea-elastomers are shown in dependence to the PDMS molecular weight.
Das forschungsgetriebene Lehrformat "Projektorientiertes Lernen" wird im Masterprogramm der Fakultät Angewandte Chemie der Hochschule Reutlingen von uns seit nunmehr einer Dekade eingesetzt und stetig weiter entwickelt. Dieses Format hat sich besonders bewährt, um methodische und fachliche Kompetenzen nachhaltig zu vermitteln. Es war uns ein Anliegen, auch anderen an der praxisorientierten Ausgestaltung der Lehre Interessierten unsere Erfahrungen mitzuteilen und unsere Vorgehensweise konkret vorzustellen. Dazu haben wir unsere bisher verwendeten Dokumente und Veröffentlichungen zu diesem Thema redigiert und stellen sie in dem vorliegenden Buch vor. In diesem von uns als "Kurshandbuch" für Anwender gedachten Werk finden sich unsere über Jahre gesammelten Erfahrungen mit der Organisation eines solchen Lehr- und Lernformats.
Structural and functional thermosetting composite materials are exposed to different kinds of stress which can damage the polymer matrix, thus impairing the intended properties. Therefore, self-healing materials have attracted the attention of many research groups over the last decades in order to provide satisfactory material properties and outstanding product durability. The present article provides a critical overview of promising self-healing strategies for crosslinked thermoset polymers. It is organized in two parts: an overview about the different approaches to self-healing is given in the first part, whereas the second part focuses on the specific chemistries of the main strategies to achieve self-healing through crosslinking. It is attempted to provide a comprehensive discussion of different approaches which are described in the scientific literature. By comparison of the advantages and disadvantages, the authors wish to provide helpful insights on the assessment of the potential to transfer the extensive present knowledge about self-healing materials and methods to surface varnishing thermoset coatings.
This article provides a general overview of the most promising candidates of bio based materials and deals with the most important issues when it comes to their incorporation into PF resins. Due to their abundance on Earth, much knowledge of lignin-based materials has already been gained and uses of lignin in PF resins have been studied for many decades. Other natural polyphenols that are less frequently considered for impregnation are covered as well, as they do also possess some potential for PF substitution.
High quality decorative laminate panels typically consist of two major types of components: the surface layers comprising décor and overlay papers that are impregnated with melamine-based resins, and the core which is made of stacks of kraft papers impregnated with phenolic (PF) resin. The PF-impregnated layers impart superior hydrolytic stability, mechanical strength and fire-resistance to the composite. The manufacturing involves the complex interplay between resin, paper and impregnation/drying processes. Changes in the input variables cause significant alterations in the process characteristics and adaptations of the used materials and specific process conditions may, in turn, be required. This review summarizes the main variables influencing both processability and technological properties of phenolic resin impregnated papers and laminates produced therefrom. It is aimed at presenting the main influences from the involved components (resin and paper), how these may be controlled during the respective process steps (resin preparation and paper production), how they influence the impregnation and lamination conditions, how they affect specific aspects of paper and laminate performance, and how they interact with each other
(synergies).
Despite the significant potential offered by the powder coating process for finishing wood-based materials, until now it has been used almost exclusively for coating Medium Density Fiber Board (MDF). A research project aims to develop processes and substrate materials that will allow lightweight boards to be powder coated.
Comments on “Solubility parameter of chitin and chitosan”, Carbohydrate Polymers 36 (1998) 121–127
(2017)
Results on the solubility parameters of chitin and chitosan presented in the paper DOI: 10.1016/S0144-8617(98)00020-4 were recalculated and data evaluation was redone. A number of misprints, erroneous calculations and data evaluations were found with respect to Hansen as well as total solubility parameters as derived according to group contribution methods by Hoftyzer-Van Krevelen and Hoy’s system. Revised numerical data are presented.
Recycling of poly(ethylene terephthalate) (PET) is of crucial importance, since worldwide amounts of PETwaste increase rapidly due to its widespread applications. Hence, several methods have been developed, like energetic, material, thermo-mechanical and chemical recycling of PET. Most frequently, PET-waste is incinerated for energy recovery, used as additive in concrete composites or glycolysed to yield mixtures of monomers and undefined oligomers. While energetic and thermo-mechanical recycling entail downcycling of the material, chemical recycling requires considerable amounts of chemicals and demanding processing steps entailing toxic and ecological issues. This review provides a thorough survey of PET-recycling including energetic, material, thermo-mechanical and chemical methods. It focuses on chemical methods describing important reaction parameters and yields of obtained reaction products. While most methods yield monomers, only a few yield undefined low molecular weight oligomers for impaired applications (dispersants or plasticizers). Further, the present work presents an alternative chemical recycling method of PET in comparison to existing chemical methods.
In der vorliegenden Studie werden typische, kommerziell erhältliche und mit unterschiedlichen Lacksystemen beschichtete MDF für den Küchenbereich hinsichtlich ihres Emissionsverhaltens und deren Oberflächeneigenschaften verglichen: wasserlack-, lösungsmittellack- und pulverlackbasierte Oberflächen. Es zeigt sich, dass eine Pulverlackierung insgesamt zu höherwertigen Produkten führt, sowohl in Bezug auf Kratzbeständigkeit, Haftung und Beständigkeit gegen feuchte Hitze als auch insbesondere in Bezug auf VOC-Emissionen. Die Wasserlackoberflächen schnitten hinsichtlich ihres Emissionsverhaltens deutlich besser ab als die lösemittelbasierten Beschichtungssysteme und zeigten in Bezug auf die Oberflächeneigenschaften mit einer Ausnahme vergleichbare Kennwerte.
Block-copolyesters of polyethylene terephthalate (PET) and polyethylene naphthalate (PEN) were synthesized via reactive extrusion. The influence of processing parameters on the material properties on a molecular scale like degree of trans-esterification, block length, and degree of randomness were investigated. The varied process factors were extrusion temperature and rotational speed. The effects of process parameter variation were investigated by 1H-NMR-spectroscopy. The experimental results show a clear dependence of the molecular properties on the processing conditions. By using statistical experimental design (DoE), it was possible to prepare defined copolyesters from PET and PEN without addition of further chemicals. With a degree of randomness between 0.05 and 0.5, the presence of an actual copolyester was confirmed when appropriate extrusion conditions were applied. The reactive extrusion process was confirmed to be suitable to produce defined block-copolyesters in a predictable and reproducible way. It was possible to produce designed sequence lengths, which could be adjusted within a range of 11–136 repeating units in the case of PET and, in the case of PEN, of 2.5–26. The produced materials can be used as barrier materials or barrier coatings to protect substrates against molecular oxygen and water vapour, e.g., in organic photovoltaic applications or food packaging. The described method is a one-pot alternative method to the previously described chemical recycling pathway.